In the last decade, research on the synthesis and characterization of nanosized ferrites has highly increased and a wide range of new applications for these materials have been identified. The ability to tailor the structure, chemical, optical, magnetic, and electrical properties of ferrites by selecting the synthesis parameters further enhanced their widespread use. The paper reviews the synthesis methods and applications of MFe₂O₄ (M = Co, Cu, Mn, Ni, Zn) nanoparticles, with emphasis on the advantages and disadvantages of each synthesis route and main applications. Along with the conventional methods like sol-gel, thermal decomposition, combustion, co-precipitation, hydrothermal, and solid-state synthesis, several unconventional methods, like sonochemical, microwave assisted combustion, spray pyrolysis, spray drying, laser pyrolysis, microemulsion, reverse micelle, and biosynthesis, are also presented. MFe₂O₄ (M = Co, Cu, Mn, Ni, Zn) nanosized ferrites present good magnetic (high coercivity, high anisotropy, high Curie temperature, moderate saturation magnetization), electrical (high electrical resistance, low eddy current losses), mechanical (significant mechanical hardness), and chemical (chemical stability, rich redox chemistry) properties that make them suitable for potential applications in the field of magnetic and dielectric materials, photoluminescence, catalysis, photocatalysis, water decontamination, pigments, corrosion protection, sensors, antimicrobial agents, and biomedicine.

The formation, structure, and thermal and magnetic properties of MFe₂O₄@SiO₂ (M = Co, Mn, Zn, Ni, Cu) (60% MFe₂O₄/40% SiO₂) nanocomposites produced by a modified sol-gel method, followed by annealing at 300, 600, 900 and 1200 °C, were studied. The thermal analysis and Fourier transform infrared spectroscopy showed the formation of metal-glyoxylates below 210 °C and their decomposition into the corresponding ferrite around 300 °C. The evolution of crystalline phases and variation of crystallite sizes differs from ferrite to ferrite and depends on the annealing temperature. The magnetic measurements revealed the dependence of saturation and remanent magnetization, coercivity, and anisotropy on ferrite type, annealing temperature, and particle size. By annealing the nanocomposites (NCs) at 1200 °C paramagnetic MnFe₂O₄, CoFe₂O₄, NiFe₂O₄ and CuFe₂O₄ and antiferromagnetic ZnFe₂O₄ are obtained.

The structural, morphological and magnetic properties of MFe₂O₄ (M = Co, Ni, Zn, Cu, Mn) type ferrites produced by thermal decomposition at 700 and 1000 °C were studied. The thermal analysis revealed that the ferrites are formed at up to 350 °C. After heat treatment at 1000 °C, single-phase ferrite nanoparticles were attained, while after heat treatment at 700 °C, the CoFe₂O₄ was accompanied by Co₃O₄ and the MnFe₂O₄ by α-Fe₂O₃. The particle size of the spherical shape in the nanoscale region was confirmed by transmission electron microscopy. The specific surface area below 0.5 m²/g suggested a non–porous structure with particle agglomeration that limits nitrogen absorption. By heat treatment at 1000 °C, superparamagnetic CoFe₂O₄ nanoparticles and paramagnetic NiFe₂O₄, MnFe₂O₄, CuFe₂O₄ and ZnFe₂O₄ nanoparticles were obtained.

This paper presents the influence of Mn²⁺ substitution by Ni²⁺ on the structural, morphological and magnetic properties of Mn_1−xNi_xFe₂O₄@SiO₂ (x = 0, 0.25, 0.50, 0.75, 1.00) nanocomposites (NCs) obtained by a modified sol-gel method. The Fourier transform infrared spectra confirm the formation of a SiO₂ matrix and ferrite, while the X-ray diffraction patterns show the presence of poorly crystalline ferrite at low annealing temperatures and highly crystalline mixed cubic spinel ferrite accompanied by secondary phases at high annealing temperatures. The lattice parameters gradually decrease, while the crystallite size, volume, and X-ray density of Mn_1−xNi_xFe₂O₄@SiO₂ NCs increase with increasing Ni content and follow Vegard’s law. The saturation magnetization, remanent magnetization, squareness, magnetic moment per formula unit, and anisotropy constant increase, while the coercivity decreases with increasing Ni content. These parameters are larger for the samples with the same chemical formula, annealed at higher temperatures. The NCs with high Ni content show superparamagnetic-like behavior, while the NCs with high Mn content display paramagnetic behavior.