Bamboo is an underutilized resource widely available in countries with rapidly developing economies. Structural bamboo products, analogous to wood products, allow flexibility in the shape and dimensions of bamboo structural members. Here, the ultrastructure, microstructure, cell wall properties and flexural properties of three species of bamboo (Moso, Guadua and Tre Gai) are compared. At a given density, the axial modulus of elasticity of Guadua is higher than that of Moso or Tre Gai, which are similar; ultrastructural results suggest that Guadua has a higher solid cell wall stiffness. At a given density, their moduli of rupture are similar.National Science Foundation (U.S.) (OISE-1258574

HCl gas hydrolysis of a bacterial cellulose (BC) aerogel followed by 2,2,6,6-tetramethylpiperidine-1-oxyl radical-mediated oxidation was used to produce hydrolyzed BC with carboxylate groups, which subsequently disintegrated into a stable dispersion of cellulose nanocrystals (CNCs). The degree of polymerization was successfully reduced from 2160 to 220 with a CNC yield of >80%.

Structural and chemical deterioration and its impact on cell wall mechanics were investigated for visually intact cell walls (VICWs) in waterlogged archaeological wood (WAW). Cell wall mechanical properties were examined by nanoindentation without prior embedding. WAW showed more than 25% decrease of both hardness and elastic modulus. Changes of cell wall composition, cellulose crystallite structure and porosity were investigated by ATR-FTIR imaging, Raman imaging, wet chemistry, ¹³C-solid state NMR, pyrolysis-GC/MS, wide angle X-ray scattering, and N₂ nitrogen adsorption. VICWs in WAW possessed a cleavage of carboxyl in side chains of xylan, a serious loss of polysaccharides, and a partial breakage of β-O-4 interlinks in lignin. This was accompanied by a higher amount of mesopores in cell walls. Even VICWs in WAW were severely deteriorated at the nanoscale with impact on mechanics, which has strong implications for the conservation of archaeological shipwrecks.

The impact of drying on the structure of the never-dried hardwood cell wall was studied at nanometer level by means of wide- and small-angle X-ray scattering (WAXS, SAXS), and at micrometer level by X-ray microtomography (μCT). Never-dried silver birch, European aspen and hybrid aspen samples were measured by WAXSin situduring drying in air. The samples included juvenile and mature wood, as well as normal and tension wood to allow comparison of the effects of different matrix compositions and microfibril angles. The deformations of cellulose crystallites and amorphous components of the cell wall were detected as changes in the cellulose reflections200and004and amorphous halo in the WAXS patterns. Especially, the width of the reflection004,corresponding to the cellulose chain direction, increased due to drying in all the samples, indicating an increase of strain and disorder of the chains. Also, the cellulose unit cell shrank 0.2–0.3% during drying in this direction in all the samples except in hybrid aspen tension wood. According to the SAXS results of silver birch, the distance between micro-fibrils decreased during drying. It was detected by μCT that the mean cross-sectional maximum width of the parenchymatous rays decreased from that of never-dried to air-dried birch by roughly 16%.