Heterogeneous photocatalysis is an advanced, efficient oxidation process that uses solar energy to be sustainable and low-cost compared to conventional wastewater treatments. This study synthesized BiOI/Fe₃O₄ using the solvothermal technique, evaluating stoichiometric ratios of Bi/Fe (2:1, 3:1, 5:1, and 7:1) under simulated solar irradiation to optimize the degradation of caffeic acid, a pollutant found in wastewater from the wine and pisco industry. The nanomaterial with a 5:1 ratio (BF-5) was the most effective, achieving a degradation of 77.2% in 180 min. Characterization by X-ray Diffraction (XRD), Transmission Electron Microscopy (TEM), Brunauer–Emmett–Teller (BET), Barrett–Joyner–Halenda (BJH), Fourier Transform Infrared Spectroscopy (FTIR), Diffuse Reflectance Spectroscopy (DRS), and Vibrating Sample Magnetometry (VSM) showed that BF-5 has a porous three-dimensional structure with BiOI nanosheets coating the Fe₃O₄ surface, while retaining the pristine BiOI properties. The magnetite provided magnetic properties that facilitated the recovery of the photocatalyst, reaching 89.4% recovery. These findings highlight the potential of BF-5 as an efficient and recoverable photocatalyst for industrial applications. The technical, economic, and environmental feasibility were also evaluated at the technological readiness level (TRL) to project solar photocatalysis in real applications.

Recently, bismuth oxyiodide (BiOI) is an attractive semiconductor to use in heterogeneous photocatalysis processes. Unfortunately, BiOI individually shows limited photocatalytic efficiency, instability, and a quick recombination of electron/holes. Considering the practical application of this semiconductor, some studies show that synthetic zeolites provide good support for this photocatalyst. This support material permits a better photocatalytic efficiency because it prevents the quick recombination of photogenerated pairs. However, the optimal conditions (time and temperature) to obtain composites (BiOI/ synthetic zeolite) with high photocatalytic efficiency using a coprecipitation-solvothermal growth method have not yet been reported. In this study, a response surface methodology (RSM) based on a central composite design (CCD) was applied to optimize the synthesis conditions of BiOI/mordenite composites. For this purpose, eleven BiOI/mordenite composites were synthesized using a combined coprecipitation-solvothermal method under different time and temperature conditions. The photocatalytic activities of the synthesized composites were evaluated after 20 min of photocatalytic oxidation of caffeic acid, a typical organic pollutant found in agro-industrial wastewater. Moreover, BiOI/mordenite composites with the highest and lowest photocatalytic activity were physically and chemically characterized using nitrogen adsorption isotherms, scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), and diffuse reflectance spectroscopy (DRS). The optimal synthesis conditions prove to be 187 °C and 9 h. In addition, the changes applied to the experimental conditions led to surface property modifications that influenced the photocatalytic degradation efficiency of the BiOI/mordenite composite toward caffeic acid photodegradation.