In designing high-performance, lightweight components, cellular structures are one of the approaches to be considered. The present study aimed to analyze the effect of the infill line distance of 3D printed circular samples on their compressive elastic behavior. Lightweight cellular poly-lactic acid (PLA) samples with a triangular infill pattern were exposed to cyclic compressive loading and their stiffness was investigated. PLA is one of the most commonly used thermoplastic materials in additive manufacturing using the fused filament fabrication (FFF) process. Cylindrical samples with a diameter of 11.42 mm and a height of 10 mm were printed using FFF technology with two different infill line distances (1.6 mm and 2.4 mm). Comparing the nominal compressive stress-nominal strain curves under cyclic loading showed that the first cycle response was significantly different with respect to the subsequent ones. Furthermore, an analysis of the dependence of the modulus of elasticity on the effects of cyclic loading was performed. It was found that through elastic deformation, and combined elastic and plastic deformation, the samples’ properties such as stiffness could be altered.

The additive technologies widely used in recent years provide enormous flexibility in the production of cellular structures. Material extrusion (MEX) technology has become very popular due to the increasing availability of relatively inexpensive desktop 3D printers and the capability of fabricating parts with complex geometries. Poly-lactic acid (PLA) is a biodegradable and commonly applied thermoplastic material in additive manufacturing (AM). In this study, using a simulation method based on the user subroutine titled “user subroutine to redefine field variables at a material point” (USDFLD) in the finite element method (FEM) ABAQUS software, the elastic stiffness (ES) of a cylindrical lightweight cellular PLA sample with a 2.4 mm infill line distance (ILD), which was designed as a layered structure similar to the laboratory mode with a MEX method and was subjected to cyclic compressive loading, was investigated by considering the variation of the Young’s modulus depending on the variation of the equivalent plastic strain (PEEQ). It was observed that the PLA sample’s elastic stiffness increases during cyclic loading. This increase is high in the initial cycles and less in the subsequent cycles. It was also observed that the simulation results are in good agreement with the experimental results.