The use of more eco-efficient cements in concretes is one of the keys to ensuring construction industry sustainability. Such eco-efficient binders often contain large but variable proportions of industrial waste or by-products in their composition, many of which may be naturally occurring radioactive materials (NORMs). This study explored the application of a new gamma spectrometric method for measuring radionuclide activity in hybrid alkali-activated cements from solid 5 cm cubic specimens rather than powder samples. The research involved assessing the effect of significant variables such as the nature of the alkaline activator, reaction time and curing conditions to relate the microstructures identified to the radiological behavior observed. The findings showed that varying the inputs generated pastes with similar reaction products (C-S-H, C-A-S-H and (N,C)-A-S-H) but different microstructures. The new gamma spectrometric method for measuring radioactivity in solid 5 cm cubic specimens in alkaline pastes was found to be valid. The variables involved in hybrid cement activation were shown to have no impact on specimen radioactive content. The powder samples, however, emanated ²²²Rn (a descendent of ²²⁶Ra), possibly due to the deformation taking place in fly ash structure during alkaline activation. Further research would be required to explain that finding.

Biomass ash is currently attracting the attention of science and industry as an inexhaustible eco-friendly alternative to pozzolans traditionally used in commercial cement manufacture (fly ash, silica fume, natural/calcined pozzolan). This paper explores a new line of research into Marabou weed ash (MA), an alternative to better-known conventional agro-industry waste materials (rice husk, bagasse cane, bamboo, forest waste, etc.) produced in Cuba from an invasive plant harvested as biomass for bioenergy production. The study entailed full characterization of MA using a variety of instrumental techniques, analysis of pozzolanic reactivity in the pozzolan/lime system, and, finally its influence on the physical and mechanical properties of binary pastes and mortars containing 10% and 20% MA replacement content. The results indicate that MA has a very low acid oxide content and a high loss on ignition (30%) and K₂O content (6.9%), which produces medium–low pozzolanic activity. Despite an observed increase in the blended mortars’ total and capillary water absorption capacity and electrical resistivity and a loss in mechanical strength approximately equivalent to the replacement percentage, the 10% and 20% MA blended cements meet the regulatory chemical, physical, and mechanical requirements specified. Marabou weed ash is therefore a viable future supplementary cementitious material.

Supplementary cementitious materials (SCMs) in industrial waste and by-products are routinely used to mitigate the adverse environmental effects of, and lower the energy consumption associated with, ordinary Portland cement (OPC) manufacture. Many such SCMs, such as type F coal fly ash (FA), are naturally occurring radioactive materials (NORMs). ²²⁶Ra, ²³²Th and ⁴⁰K radionuclide activity concentration, information needed to determine what is known as the gamma-ray activity concentration index (ACI), is normally collected from ground cement samples. The present study aims to validate a new method for calculating the ACI from measurements made on unground 5 cm cubic specimens. Mechanical, mineralogical and radiological characterisation of 28-day OPC + FA pastes (bearing up to 30 wt % FA) were characterised to determine their mechanical, mineralogical and radiological properties. The activity concentrations found for ²²⁶Ra, ²¹²Pb, ²³²Th and ⁴⁰K in hardened, intact 5 cm cubic specimens were also statistically equal to the theoretically calculated values and to the same materials when ground to a powder. These findings consequently validated the new method. The possibility of determining the activity concentrations needed to establish the ACI for cement-based materials on unground samples introduces a new field of radiological research on actual cement, mortar and concrete materials.

This research paper provides new insights into the impact of accelerated mineralization of alkaline waste materials on the physical and mechanical behavior of low-carbon cement-based mortars. Standardized eco-cement mortars were prepared by replacing Portland cement with 7% and 20% proportions of three alkaline waste materials (white ladle furnace slag, biomass ash, and fine concrete waste fraction) that had been previously carbonated in a static reactor at predefined humidity and CO₂ concentration. The mortars’ physical (total/capillary water absorption, electrical resistivity) and mechanical properties (compressive strength up to 90 d of curing) were analyzed, and their microstructures were examined using mercury intrusion porosimetry and computed tomography. The results reveal that carbonated waste materials generate a greater heat of hydration and have a lower total and capillary water absorption capacity, while the electrical resistivity and compressive strength tests generally indicate that they behave similarly to mortars not containing carbonated minerals. Mercury intrusion porosimetry (microporosity) indicates an increase in total porosity, with no clear refinement versus non-carbonated materials, while computed tomography (macroporosity) reveals a refinement of the pore structure with a significant reduction in the number of larger pores (>0.09 mm³) and intermediate pores (0.001–0.09 mm³) when carbonated residues are incorporated that varies depending on waste material. The construction and demolition waste (CCDW-C) introduced the best physical and mechanical behavior. These studies confirm the possibility of recycling carbonated waste materials as low-carbon supplementary cementitious materials (SCMs).

The study reported the effect of granite sand on strength and microstructural developments in mortars prepare from OPC with a high coal fly ash (FA) content or from hybrid alkaline cements. The radiological behaviour of the resulting mortars was compared to materials prepared with siliceous sand (with particles sizes of 0.96, which would ultimately limit their use. A conclusion of interest is that where information is at hand on the starting materials (OPC, FA, sand, admixtures), their proportions in the mortar and the mixing liquid content (water or alkaline activators) their radiological content is accurately predicted. The inference is that a mortar’s radiological content and ACI can be known prior to mixing, providing a criterion for determining its viability. That in turn lowers environmental risks and the health hazards for people in contact with such materials.

Using CO₂-mineralised alkaline waste as a supplementary cementitious material has the potential to advance sustainable construction practices. This paper evaluates the effect of carbonating three fine industrial waste materials—construction and demolition waste, ladle furnace slag, and biomass ash—on the durability performance of blended cements in which they replace 7% and 20% of ordinary Portland cement. The performance of carbonated waste was compared with that of their non-carbonated counterparts through chloride ingress resistance, a key parameter governing reinforcement corrosion. The results show that prior carbonation can significantly influence chloride transport properties, although the magnitude and direction of the effect depend strongly on the waste type and replacement level. Mortars with carbonated construction and demolition waste or ladle furnace slag generally reduced the chloride diffusion coefficient compared with the corresponding non-carbonated materials. This behaviour was associated with greater portlandite consumption and enhanced chloride-binding capacity. Nevertheless, none of the blended systems outperformed the ordinary Portland cement (OPC ) in terms of chloride diffusion resistance. Conversely, biomass ash at 20% replacement led to markedly reduced performance, with the estimated time to steel depassivation decreasing to 1–2 years under the exposure conditions considered. These findings indicate that prior carbonation may improve the suitability of some wastes for cementitious applications relative to their non-carbonated counterparts, although the resulting chloride resistance remains lower than that of OPC. The benefits are of waste carbonation are therefore material-dependent and should be assessed on a case-by-case basis.