The reduced form of graphene oxide (r-GO) represents a versatile precursor to obtain graphene derivatives. Graphene oxide (GO) consists of a layered material based on a carbon skeleton functionalized by different oxygen-containing groups, while r-GO is obtained by the almost complete removal of these oxygen-containing functional groups. The r-GO has mechanical, electrical, and optical properties quite similar to graphene, thus, it proves to be a convenient 2D material useful for many technological applications. Nowadays, the most important aspects to consider in producing r-GO are: (i) the possibility of obtaining the highest reduction grade; (ii) the possibility of improving the dispersion stability of the resulting graphene using surfactants; (iii) the use of environmentally friendly and inexpensive reducing agents. Consequently, the availability of effective soft-chemistry approaches based on a green reducing agent for converting GO to r-GO are strongly needed. Among the green reductants, the most suitable is L-ascorbic acid (L-aa). Different studies have revealed that L-aa can achieve C/O ratio and conductivity values comparable to those obtained by hydrazine, a typical reducing agent. These aspects could promote an effective application strategy, and for this reason, this review summarizes and analyzes, in some detail, the up-to date literature on the reduction of GO by L-aa. The results are organized according to the two most important approaches, which are the reduction in liquid-phase, and the reduction in gel-phase. Reaction mechanisms and different experimental parameters affecting the processes were also compared.

Graphene oxide (GO) and its reduced form (rGO) have recently attracted a fascinating interest due to their physico-chemical properties, which have opened up new and interesting opportunities in a wide range of biomedical applications, such as wound healing. It is worth noting that GO and rGO may offer a convenient access to its ready dispersion within various polymeric matrices (such as cellulose and its derivative forms), owing to their large surface area, based on a carbon skeleton with many functional groups (i.e., hydroxyl, carboxyl, epoxy bridge, and carbonyl moieties). This results in new synergic properties due to the presence of both components (GO or rGO and polymers), acting at different length-scales. Furthermore, they have shown efficient antimicrobial and angiogenic properties, mostly related to the intracellular formation of reactive oxygen species (ROS), which are advantageous in wound care management. For this reason, GO or rGO integration in cellulose-based matrixes have allowed for designing highly advanced multifunctional hybrid nanocomposites with tailored properties. The current review aims to discuss a potential relationship between structural and physico-chemical properties (i.e., size, edge density, surface chemistry, hydrophilicity) of the nanocomposites with antimicrobials and angiogenic mechanisms that synergically influence the wound healing phenomenon, by paying particular attention to recent findings of GO or rGO/cellulose nanocomposites. Accordingly, after providing a general overview of cellulose and its derivatives, the production methods used for GO and rGO synthesis, the mechanisms that guide antimicrobial and angiogenic processes of tissue repair, as well as the most recent and remarkable outcomes on GO/cellulose scaffolds in wound healing applications, will be presented.

The Hummers’ method for graphite oxide (GO) preparation has been applied to graphite nanoplatelets, in order to achieve higher reaction yield and faster kinetics. Aqueous GO solutions have been used to produce uniform GO films on a polyethylene terephthalate substrate, generating graphene patterns in a controlled way (widths of a few tens of microns). The reduction of GO deposited on the polymeric substrate has been performed by using a Nd:YVO ₄ continuous-wave frequency-duplicated laser. Spectroscopic and diffractometric characterizations (FT-IR, visible-NIR, Raman, XPS, and XRD) have shown that the reduction process induced by the laser annealing technique is mainly due to dehydration of the GO layers. It has been obtained by means of a suitable laser optical apparatus, a controlled reduction of GO without damaging the substrate, and precise writing of micro-tracks that can be used as electrically and thermally conductive patterns.

An extension of the Mie [Ann. Phys. 25, 377 (1908)] theory for the calculation of optical absorption spectra in bimetallic nanoparticles has been developed. The nanoparticle dielectric function is assumed to be a weighted linear combination of dielectric functions for single particles. Accordingly, analytical expressions for the resonance light absorption frequency, the spectrum maximum value, and the full width at half maximum have been derived, taking into account the interband transitions in the dielectric functions. Experiments have been performed on polymer-embedded Ag∕Au nanoparticles prepared by reducing the presence of poly(vinyl pyrrolidone) at room temperature. Experimental absorption spectra have been compared to numerical curves derived by the model in the case of Ag∕Au systems at different relative compositions, and they are in good agreement. The time dependence of both Ag∕Au nanoparticle size and chemical composition during the growth process has also been investigated.

A simple approach for the bulk production of carbon nanoscrolls (CNSs) is described. This method is based on the application of shear-friction forces to convert graphite nanoplatelets into carbon nanoscrolls using a bi-axially oriented polypropylene (BOPP) surface. The combined action of shear and friction forces causes the exfoliation of graphite nanoplatelets and the simultaneous roll-up of graphite layers. Evidence of the CNS formation is given by optical microscopy, scanning electron microscopy, and transmission electron microscopy. These investigations reveal that the CNSs have a long tube-like and fusiform structure with a hollow core surrounded by few layers of graphene. Micro-Raman spectroscopy shows that the produced structures are not defect free, and optical spectroscopy reveals distinctive features due to the presence of two weak absorption bands at 224 and 324 nm.