As a typical third-generation semiconductor material, silicon carbide (SiC) has been increasingly used in recent years. However, the outstanding performance of SiC component can only be obtained when it has a high-quality surface and low-damage subsurface. Due to the hard–brittle property of SiC, it remains a challenge to investigate the ductile machining mechanism, especially at the nano scale. In this study, a three-dimensional molecular dynamics (MD) simulation model of nanometric cutting on monocrystalline 3C-SiC was established based on the ABOP Tersoff potential. Multi-group MD simulations were performed to study the removal mechanism of SiC at the nano scale. The effects of both cutting speed and undeformed cutting thickness on the material removal mechanism were considered. The ductile machining mechanism, cutting force, hydrostatic pressure, and tool wear was analyzed in depth. It was determined that the chip formation was dominated by the extrusion action rather than the shear theory during the nanocutting process. The performance and service life of the diamond tool can be effectively improved by properly increasing the cutting speed and reducing the undeformed cutting thickness. Additionally, the nanometric cutting at a higher cutting speed was able to improve the material removal rate but reduced the quality of machined surface and enlarged the subsurface damage of SiC. It is believed that the results can promote the level of ultraprecision machining technology.

Ni-based composite coating containing nanodiamonds was deposited on the substrate of Q235A low-carbon steel in a traditional Watts solution, without any additive. The nanodiamond grains prepared by detonation synthesis were measured by Transmission electron microscope (TEM) and X-ray diffraction (XRD). The electrochemical behavior of Ni²⁺ ion in the composite bath including nanodiamonds was studied by linear sweep voltammetry experiments, and the morphology, elastic modulus, and hardness of Ni-based composite coating were characterized using Scanning Electron microscope (SEM) and the nano-indenter XP tester. Effects of the nanodiamond concentration in the bath, stirring speed, and the electroplate mode on the properties of Ni-based composite coating were investigated. The results show that the reduction of Ni²⁺ ion in the electroplating process increased initially, and then decreased as the nanodiamond concentration in the bath increased from 4 g/L to 16 g/L, irrespective of whether direct current (DC), single-pulse, or double-pulse electroplating mode was used. The highest over-potential could be obtained when the nanodiamond concentration in the bath was 8 g/L. Moreover, the hardness and elastic modulus of the composite coating prepared by the DC electroplating mode were 4.68 and 194.30 GPa, respectively. By using the same plating parameters, the coating prepared by the double-pulse electroplating mode showed better properties, with hardness and elastic modulus values of 5.22 and 197.38 GPa, respectively.