Fe₃O₄@SiO₂ core-shell nanoparticles (NPs) were synthesized with the co-precipitation method and functionalized with NH₂ amino-groups. The nanoparticles were characterized by X-ray, FT-IR spectroscopy, transmission electron microscopy, selected area electron diffraction, and vibrating sample magnetometry. The magnetic core of all the nanoparticles was shown to be nanocrystalline with the crystal parameters corresponding only to the Fe₃O₄ phase covered with a homogeneous amorphous silica (SiO₂) shell of about 6 nm in thickness. The FT-IR spectra confirmed the appearance of chemical bonds at amino functionalization. The magnetic measurements revealed unusually high saturation magnetization of the initial Fe₃O₄ nanoparticles, which was presumably associated with the deviations in the Fe ion distribution between the tetrahedral and octahedral positions in the nanocrystals as compared to the bulk stoichiometric magnetite. The fluorescent spectrum of eosin Y-doped NPs dispersed in water solution was obtained and a red shift and line broadening (in comparison with the dye molecules being free in water) were revealed and explained. Most attention was paid to the adsorption properties of the nanoparticles with respect to three dyes: methylene blue, Congo red, and eosin Y. The kinetic data showed that the adsorption processes were associated with the pseudo-second order mechanism for all three dyes. The equilibrium data were more compatible with the Langmuir isotherm and the maximum adsorption capacity was reached for Congo red.

This work is devoted to the study of magnetic Fe₃O₄ nanoparticles doubly coated with carbon. First, Fe₃O₄@C nanoparticles were synthesized by thermal decomposition. Then these synthesized nanoparticles, 20–30 nm in size were processed in a solution of glucose at 200 °C during 12 h, which led to an unexpected phenomenon—the nanoparticles self-assembled into large conglomerates of a regular shape of about 300 nm in size. The morphology and features of the magnetic properties of the obtained hybrid nanoparticles were characterized by transmission electron microscopy, differential thermo-gravimetric analysis, vibrating sample magnetometer, magnetic circular dichroism and Mössbauer spectroscopy. It was shown that the magnetic core of Fe₃O₄@C nanoparticles was nano-crystalline, corresponding to the Fe₃O₄ phase. The Fe₃O₄@C@C nanoparticles presumably contain Fe₃O₄ phase (80%) with admixture of maghemite (20%), the thickness of the carbon shell in the first case was of about 2–4 nm. The formation of very large nanoparticle conglomerates with a linear size up to 300 nm and of the same regular shape is a remarkable peculiarity of the Fe₃O₄@C@C nanoparticles. Adsorption of organic dyes from water by the studied nanoparticles was also studied. The best candidates for the removal of dyes were Fe₃O₄@C@C nanoparticles. The kinetic data showed that the adsorption processes were associated with the pseudo-second order mechanism for cationic dye methylene blue (MB) and anionic dye Congo red (CR). The equilibrium data were more consistent with the Langmuir isotherm and were perfectly described by the Langmuir–Freundlich model.

The mechanism of room temperature (RT) ferromagnetism for low doping concentration of 2.5% V in ZnO have been systematically discussed by measuring structural, electrical, and magnetic properties. The evolution of the Curie temperature from above RT in insulated V:ZnO powders to 270 K in semiconducting samples was observed with increasing carrier concentration by using different hydrogenated annealing treatment. The results provide a direct observation that the free carriers suppress the ferromagnetism and might be associated the phenomena of charge-transfer and interaction between bound magnetic polarons.

Nearly monodisperse CuCr(2)Se(4) hexagon-shaped nanoparticles with crystallite sizes from 15.1 to 24.3 nm were synthesized by thermal decomposition of metal chlorides and selenium powder in oleylamine. In addition, the 'flower'-shaped CuCr(2)Se(4) nanoparticles with a crystallite size 19.8 nm were also fabricated under similar conditions using heptanoic acid. Magnetic measurements show that all samples reveal ferromagnetic behavior below 350 K. The 'flower'-shaped nanoparticles have saturation magnetization, coercivity and remanent magnetization higher than the hexagon-shaped nanoparticles. However, the Curie temperature of the 'flower'-shaped nanoparticles (approximately 380 K) is somewhat lower than in the hexagon-shaped nanoparticles (420-430 K). These phenomena may be associated with the shape and surface anisotropy which would exert a tremendous influence on the particle's magnetic properties.