Intumescent fire-retardant coatings, which feature thinner layers and good decorative effects while significantly reducing heat transfer and air dispersion capabilities, are highly attractive for fire safety applications due to their effective prevention of material combustion and protection of materials. Particularly, the worldwide demand for improved environmental protection requirements has given rise to the production of waterborne intumescent fire-retardant polymer composite coatings, which are comparable to or provide more advantages than solvent-based intumescent fire-retardant polymer composite coatings in terms of low cost, reduced odor, and minimal environmental and health hazards. However, there is still a lack of a comprehensive and in-depth overview of waterborne intumescent fire-retardant polymer composite coatings. This review aims to systematically and comprehensively discuss the composition, the flame retardant and heat insulation mechanisms, and the practical applications of waterborne intumescent fire-retardant polymer composite coatings. Finally, some key challenges associated with waterborne intumescent fire-retardant polymer composite coatings are highlighted, following which future perspectives and opportunities are proposed.

Silicone rubber (SR), as one kind of highly valuable rubber material, has been widely used in many fields, e.g., construction, transportation, the electronics industry, automobiles, aviation, and biology, owing to its attractive properties, including high- and low-temperature resistance, weathering resistance, chemical stability, and electrical isolation, as well as transparency. Unfortunately, the inherent flammability of SR largely restricts its practical application in many fields that have high standard requirements for flame retardancy. Throughout the last decade, a series of flame-retardant strategies have been adopted which enhance the flame retardancy of SR and even enhance its other key properties, such as mechanical properties and thermal stability. This comprehensive review systematically reviewed the recent research advances in flame-retarded SR materials and summarized and introduced the up-to-date design of different types of flame retardants and their effects on flame-retardant properties and other performances of SR. In addition, the related flame-retardant mechanisms of the as-prepared flame-retardant SR materials are analyzed and presented. Moreover, key challenges associated with these various types of FRs are discussed, and future development directions are also proposed.

A novel and hierarchical hybrid composite (MnO₂@CHS@SA@Ni) was synthesized utilizing manganese dioxide (MnO₂) nanosheets as the core structure, self-assembly chitosan (CHS), sodium alginate (SA) and nickel species (Ni) as surface layers, and it was further incorporated into an epoxy matrix for achieving fire hazard suppression via surface self-assembly technology. Herein, the resultant hybrid epoxy composite possessed an exceptional nano-barrier and synergistic charring effect to aid the formation of a compact layered structure that enhanced its fire-resistive effectiveness. As a result, the addition of only 2 wt% MnO₂@CHS@SA@Ni hybrids led to a dramatic reduction in the peak heat release rate and total heat release values (by ca. 33% and 27.8%) of the epoxy matrix. Notably, the peak smoke production rate and total smoke production values of EP/MnO₂@CHS@SA@Ni 2% were decreased by ca. 16.9 and 38.4% compared to the corresponding data of pristine EP. This was accompanied by the suppression of toxic CO, NO release and the diffusion of thermal pyrolysis gases during combustion through TG-IR results. Overall, a significant fire-testing outcome of the proposed hierarchical structure was proven to be effective for epoxy composites in terms of flammability, smoke and toxicity reductions, optimizing their prospects in other polymeric materials in the respective fields.