There is a growing interest in using additive manufacturing to produce smart structures, which have the capability to respond to thermal and mechanical stimuli. In this report, Selective Laser Melting (SLM) is used to build a Negative Poisson's Ratio (NPR) TiNi-based Shape Memory Alloy (SMA) structure, creating a multi-functional structure that could be used as reusable armour. The study assesses the influence of SLM process parameters (laser power, scan speed, and track spacing) on the microstructural and structural integrity development in a Ti-rich TiNi alloy, as well as the impact of the post-process homogenisation treatment on the microstructure and phase transformations. The builds generally shows stress-induced cracks and residual porosity, which could be minimised through process optimisation. Nonetheless, the homogenisation treatment is essential to reduce the fraction of Ti2Ni intermetallics, which are known to disturb the B19′-chemistry, and hence the required phase transformation temperatures. The optimum process parameters are finally used to fabricate NPR structures, which were mechanically tested to validate the Poisson's ratio predictions. A higher ductility was observed in the structures that have undergone the homogenisation treatment

Recent advances in additive manufacturing (AM) have attracted significant industrial interest. Initially, AM was mainly associated with the fabrication of prototypes, but the AM advances together with the broadening range of available materials, especially for producing metallic parts, have broaden the application areas and now the technology can be used for manufacturing functional parts, too. Especially, the AM technologies enable the creation of complex and topologically optimised geometries with internal cavities that were impossible to produce with traditional manufacturing processes. However, the tight geometrical tolerances along with the strict surface integrity requirements in aerospace, biomedical and automotive industries are not achievable in most cases with standalone AM technologies. Therefore, AM parts need extensive post-processing to ensure that their surface and dimensional requirements together with their respective mechanical properties are met. In this context, it is not surprising that the integration of AM with post-processing technologies into single and multi set-up processing solutions, commonly referred to as hybrid AM, has emerged as a very attractive proposition for industry while attracting a significant R&D interest. This paper reviews the current research and technology advances associated with the hybrid AM solutions. The special focus is on hybrid AM solutions that combine the capabilities of laser-based AM for processing powders with the necessary post-process technologies for producing metal parts with required accuracy, surface integrity and material properties. Commercially available hybrid AM systems that integrate laser-based AM with post-processing technologies are also reviewed together with their key application areas. Finally, the main challenges and open issues in broadening the industrial use of hybrid AM solutions are discussed.