Additive manufacturing is catalyzing a new class of volumetrically varying lattice structures in which the dynamic mechanical response can be tailored for a specific application. Simultaneously, a diversity of materials is now available as feedstock including elastomers, which provide high viscoelasticity and increased durability. The combined benefits of complex lattices coupled with elastomers is particularly appealing for anatomy-specific wearable applications such as in athletic or safety equipment. In this study, Siemens’ DARPA TRADES-funded design and geometry-generation software, Mithril, was leveraged to design vertically-graded and uniform lattices, the configurations of which offer varying degrees of stiffness. The designed lattices were fabricated in two elastomers using different additive manufacturing processes: (a) vat photopolymerization (with compliant SIL30 elastomer from Carbon) and (b) thermoplastic material extrusion (with Ultimaker™ TPU filament providing increased stiffness). Both materials provided unique benefits with the SIL30 material offering compliance suitable for lower energy impacts and the Ultimaker™ TPU offering improved protection against higher impact energies. Moreover, a hybrid lattice combination of both materials was evaluated and demonstrated the simultaneous benefits of each, with good performance across a wider range of impact energies. This study explores the design, material, and process space for manufacturing a new class of comfortable, energy-absorbing protective equipment to protect athletes, consumers, soldiers, first responders, and packaged goods.

Polyetheretherketone (PEEK) has been the focus of substantial additive manufacturing research for two principal reasons: (a) the mechanical performance approaches that of aluminum at relatively high temperatures for thermoplastics and (b) the potential for qualification in both the aerospace and biomedical industries. Although PEEK provides outstanding strength and thermal stability, printing can be difficult due to the high melting point. Recently, high-temperature soluble support has enabled the printing of lattices and stochastic foams with overhanging features in these high-performance carbon fiber thermoplastics, in which density can be optimized to strike a balance between weight and strength to enhance performance in applications such as custom implants or aerospace structures. Although polymer powder bed fusion has long been capable of the combination of these geometries and materials, material extrusion with high-temperature sacrificial support is dramatically less expensive. This research provides a comprehensive mechanical analysis and CT-scan-based dimensional study of carbon fiber PEEK lattice structures enabled with high-temperature support and including model validation.

This work provides a structural analysis of small-scale 3D-printed wind turbine ribs subjected to compression. The ribs were manufactured according to NACA 23015 and NACA 633618 geometries, with polylactic acid (PLA) and polylactic acid with carbon fiber additives (CF-PLA). In addition, holes were manufactured into the sample bodies by either 3D printing or drilling for being compared with solid samples. The compression testing was performed by following the ASTM 695D standard, whereas the beginning and propagation of delamination were assessed with the ASTM 5528 standard. Experimental results revealed that 3D-printed built-in holes provided higher compression strength, hence higher structural efficiency, than the drilled samples. Significant improvement by adding carbon fiber additives into the PLA resin system in comparison to raw PLA was detected for at least one of the studied airfoil profiles. NACA geometries also represented a key parameter for avoiding stress concentration areas, as the FEM modeling supported. However, in damaged areas, fracture mechanisms were observed such as bead-bridging, which is a key parameter in reinforcing and consolidating the specimen bodies. Working in better interphase bonding and different additives between beads and layers is highly suggested for future studies.