In this study, the structure, electrical and thermal properties of ten polymer compositions based on polylactic acid (PLA), low-cost industrial graphene nanoplates (GNP) and multi-walled carbon nanotubes (MWCNT) in mono-filler PLA/MWCNT and PLA/GNP systems with 0–6 wt.% filler content were investigated. Filler dispersion was further improved by combining these two carbon nanofillers with different geometric shapes and aspect ratios in hybrid bi-filler nanocomposites. Scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Raman spectroscopy exhibited uniform dispersion of nanoparticles in a polymer matrix. The obtained results have shown that for the mono-filler systems with MWCNT or GNP, the electrical conductivity increased with decades. Moreover, a small synergistic effect was observed in the GNP/MWCNT/PLA bi-filler hybrid composites when combining GNP and CNT at a ratio of 3% GNP/3% CNT and 1.5% GNP:4.5% CNT, showing higher electrical conductivity with respect to the systems incorporating individual CNTs and GNPs at the same overall filler concentration. This improvement was attributed to the interaction between CNTs and GNPs limiting GNP aggregation and bridging adjacent graphene platelets thus, forming a more efficient network. Thermal conductivity increases with higher filler content; this effect was more pronounced for the mono-filler composites based on PLA and GNP due to the ability of graphene to better transfer the heat. Morphological analysis carried out by electron microscopy (SEM, TEM) and Raman indicated that the nanocomposites present smaller and more homogeneous filler aggregates. The well-dispersed nanofillers also lead to a microstructure which is able to better enhance the electron and heat transfer and maximize the electrical and thermal properties. The obtained composites are suitable for the production of a multifunctional filament with improved electrical and thermal properties for different fused deposition modelling (FDM) 3D printing applications and also present a low production cost, which could potentially increase the competitiveness of this promising market niche.

Poly(lactic acid)/graphene and poly(lactic acid)/carbon nanotube nanocomposites were prepared by an easy and low-cost method of melt blending of preliminary grinded poly(lactic acid) (PLA) with nanosized carbon fillers used as powder. Morphological, structural and mechanical properties were investigated to reveal the influence of carbon nanofiller on the PLA–based composite. The dependence of tensile strength on nanocomposite loading was defined by a series of experiments over extruded filaments using a universal mechanical testing instrument. The applying the XRD technique disclosed that compounds crystallinity significantly changed upon addition of multi walled carbon nanotubes. We demonstrated that Raman spectroscopy can be used as a quick and unambiguous method to determine the homogeneity of the nanocomposites in terms of carbon filler dispersion in a polymer matrix.

In this study, the effects of three processing stages: filament extrusion, 3D printing (FDM), and hot-pressing are investigated on electrical conductivity and tensile mechanical properties of poly(lactic) acid (PLA) composites filled with 6 wt.% of multiwall carbon nanotubes(MWCNTs), graphene nanoplatelets (GNPs), and combined fillers. The filaments show several decades’ higher electrical conductivity and 50–150% higher values of tensile characteristics, compared to the 3D printed and the hot-pressed samples due to the preferential orientation of nanoparticles during filament extrusion. Similar tensile properties and slightly higher electrical conductivity are found for the hot-pressed compared to the 3D printed samples, due to the reduction of interparticle distances, and consequently, the reduced tunneling resistances in the percolated network by hot pressing. Three structural types are observed in nanocomposite filaments depending on the distribution and interactions of fillers, such as segregated network, homogeneous network, and aggregated structure. The type of structural organization of MWCNTs, GNPs, and combined fillers in the matrix polymer is found determinant for the electrical and tensile properties. The crystallinity of the 3D printed samples is higher compared to the filament and hot-pressed samples, but this structural feature has a slight effect on the electrical and tensile properties. The results help in understanding the influence of processing on the properties of the final products based on PLA composites.

Electromagnetic and thermal properties of a non-conventional polymer nanocomposite based on thermoplastic Polylactic acid (PLA, Ingeo™) filled, in different weight percentage, with multi-walled carbon nanotubes (MWCNTs), graphene nanoplatelets (GNPs), as well as a mixture of both fillers (MWCNTs/GNPs), are analyzed. The combination of notable electrical, thermal, and electromagnetic (EM) properties of the carbon fillers, in concentrations above the percolation threshold, together with the good processability of the PLA matrix gives rise to innovative filaments for 3D printing. In particular, the shielding efficiency (SE) in the frequency range 26–37 GHz of samples increases from 0.20 dB of unfilled PLA up to 13.4 dB for composites containing MWCNTs and GNPs, corresponding to 4% and 95% of SE, respectively. The thermal conductivity of the PLA loaded with 12 wt % of GNPs is 263% higher than that of the unfilled polymer, whereas an improvement of about 99% and 190% is detected for the PLA matrix loaded with MWCNTs and both fillers, respectively. The EM and thermal characterization is combined with a morphological investigation allowing us to correlate the dispersion states of the fillers within the polymer matrix with the observed EM and thermal properties. The EM and thermal characteristics exhibited by the nanocomposites make them suitable for packaging applications of electronic devices with electromagnetic interference (EMI) shielding and thermal dissipation features.

The limitation of poor mechanical stability and difficulties in printing electrically conductive components can be overcome owing to the recent introduction of nanotechnology into the field of additive manufacturing (AM) and the consequent development of nonconventional polymer nanocomposites suitable for 3D printing. In the present work, different weight percentages (up to 6 wt % in total) of carbon-based nanostructures—multiwalled carbon nanotubes (MWCNTs), graphene nanoplatelets (GNPs), and a combination of both fillers (MWCNTs/GNPs)—were incorporated into poly(lactic) acid (PLA, Ingeo™) in an attempt to overcome several limitations of conventional 3D manufacturing based on insulating materials. Solution blending and melt mixing were the two fabrication methods adopted for preparation of the samples under test. A comparison of the morphological, rheological, and electrical properties of the resulting nanocomposites was carried out. Moreover, for the same weight concentrations, the influence of physical and geometrical features (i.e., functionalization and aspect ratio) of the embedded fillers was also investigated. Rheological methods were applied to control the quality of fillers dispersion in PLA matrix. The rheological percolation threshold was considered as reference in order to evaluate the internal structure of nanodispersions. TEM visualization, combined with rheological characterizations, was used for efficient control of the nanofiller dispersion. DC characterization revealed that lower electrical percolation thresholds and higher values of electrical conductivity were achieved using fillers with a larger aspect ratio and melt mixing, respectively. Moreover, given the possibility of obtaining complex and appropriate shapes for electromagnetic compatibility (EC) applications, electromagnetic (EM) response of the nanocomposites at the highest filler concentration was investigated in GHz and THz regions. It was found that the electromagnetic shielding efficiency (EMI) of nanocomposites strongly depended on the aspect ratio of the nanofillers, whereas the type of processing technique did not have a significant effect. Therefore, a careful choice of methods and materials must be made to address the final application for which these materials and further 3D printed architectures are designed.