Dental ceramic restorations are widely spread nowadays due to their aesthetics and biocompatibility. In time, the colour and structure of these ceramic materials can be altered by aging processes. How does artificial aging affect the optical and surface roughness of ceramics? This study aims to assess the effect of thermocycling, surface treatments and microstructure upon translucency, opalescence and surface roughness on CAD-CAM and heat-pressed glass-ceramic. Forty-eight samples (1.5 mm thickness) were fabricated from six types of A2 MT ceramic: heat-pressed and milled glass-ceramic (feldspathic, lithium disilicate and zirconia reinforced lithium silicate). The samples were obtained respecting the manufacturer’s instructions. The resulted surfaces (n = 96) were half glazed and half polished. The samples were subjected to thermocycling (10,000 cycles) and roughness values (Ra and Rz), colour coordinates (L*, a*, b*) and microstructural analyses were assessed before and after thermocycling. Translucency (TP) and opalescence (OP) were calculated. Values were statistically analysed using ANOVA test (one way). TP and OP values were significantly different between heat-pressed and milled ceramics before and also after thermocycling (p < 0.001). Surface treatments (glazing and polishing) had a significant effect on TP and OP and surface roughness (p < 0.05). The heat-pressed and milled zirconia reinforced lithium silicate glass-ceramic experienced a loss in TP and OP. Ra and Rz increased for the glazed samples, TP and OP decreased for all the samples after thermocycling. Microstructural analyse revealed that glazed surfaces were more affected by the thermocycling and especially for the zirconia reinforced lithium silicate ceramic. Optical properties and surface roughness of the chosen ceramic materials were affected by thermocycling, surface treatments and microstructural differences. The least affected of the ceramics was the lithium disilicate ceramic heat-pressed polished and glazed.

(1) Background: Thermoplastic materials are not inert and subject to changes in the oral environment, which affect their surface quality. Color stability and topographic characteristics of clear thermoplastic appliances are critical considerations. The study aimed to evaluate the optical changes and surface topography of different thermoplastic materials related to staining beverages and cleaning agents. (2) Methods: Thermoplastic polyethylene terephthalate glycol (PET-G) material specimens were selected for the study: S (Duran, Scheu-Dental GmbH, Iserlohn, Germany), D (Biolon, Dreve Dentamid GmbH, Unna, Germany), and B (Crystal, Bio Art Dental Equipment, Sao Carlos, Brazil). Four different media were involved for immersion: coffee (C) and black tea (T) at 55 °C, Coca-Cola (K) at 5 °C, and distilled water (W) at 22 °C. As for cleaning, chemical options and mechanical brushing were selected (P-powder, T-tablets, and X-brushing). Color changes, and mean surface roughness were measured at 24 h, 48 h, and after 7 days. Statistical analysis was performed. After the testing period, atomic force microscopy (AFM) analyses and SEM images were registered in order to characterize the surface topography. (3) Results: Quantitative color change evaluations revealed a slight change in color after 24 h and an extremely marked change after 48 h, respective 7 days. Mean roughness values are kept below the clinically acceptable limit of 0.20 µm for all samples. Related to mean nanoroughness values Sa, and 3D evaluations of the surface quality, Biolon samples have demonstrated the most constant behavior, while Crystal samples are visibly influenced by water immersion. Related to the cleaning method, the topography of Duran samples was influenced by mechanical brushing. (4) Conclusions: Nanoscale investigations provided high accuracy and more realistic surface quality examinations of the examined samples compared to profilometry. Both SEM and AFM should be used for a more detailed description of the surface topography.

The accuracy of newly developed ceramic materials is still being studied. Marginal and internal adaptation are known factors that have an essential impact on the long term success of dental restorations. The aim of this in vitro study was to evaluate the marginal and internal fit of heat-pressed and milled monolithic glass-ceramic restorations based on their ceramic type, processing technique, and in vitro thermocycling. Thirty-two crowns were studied and divided into four groups (n = 8), according to the ceramic material (feldspathic glass-ceramic (F) and zirconia reinforced lithium silicate glass-ceramic (ZLS)) and to their technological obtaining processes (milling (M) and heat-pressing (P)). A typodont preparation was scanned with a D2000 3D scanner to obtain identical 32 resin 3D-printed abutment teeth. Marginal and internal gaps were measured using the silicone replica technique under 40× magnification. The crowns were further cemented and thermally aged for 10,000 cycles After cementation and thermocycling of the samples, marginal and internal gaps were assessed using micro-CT (micro-computed tomography)) analysis. Data were statistically analyzed using statistical tests. Significant differences were found before and after cementation and thermocycling among the tested materials (p < 0.05). Related to technological processing, significant differences were seen in the marginal area between FP and FM (p < 0.05) Significant differences were also found in the axial and occlusal areas between the ZLSP and ZLSM. Thermocycling and cementation did not have a significant effect on the tested materials (p < 0.05). The technological processes influenced the marginal and internal fit of the crowns in favor of the CAD/CAM (computer aided design/computer aided manufacturing)technologies. Thermal aging had little effect on marginal adaptability; it increased the values for all the tested samples in a small way, but the values remained in their clinically acceptable range for all of the crowns.

(1) Background: The study was undertaken to evaluate the surface characteristics, microhardness, and color stability of PEEK materials related to water saturation and in vitro aging. (2) Methods: Custom specimens of unmodified and modified PEEK CAD/CAM materials were investigated: BioHPP, a ceramic reinforced PEEK, and Finoframe PEEK and Juvora medical PEEK, 100% PEEK materials. Forty-eight plates were sectioned in rectangular slices. The specimens were immersed in distilled water at 37 °C for a period of 28 days, and then subjected to aging by thermal cycling (10,000 cycles). Surface roughness was measured with a contact profilometer; nanosurface topographic characterization was made by Atomic Force Microscopy; Vickers hardness measurements were performed with a micro-hardness tester; color changes were calculated. All registrations were made before immersion in water and then subsequently once a week for 4 weeks, and after thermocycling. (3) Results: The studied reinforced and unfilled PEEK materials reached water saturation after the first week of immersion, without significant differences between them. The most affected from this point of view was the reinforced PEEK material. Thermocycling induces a significant increase inmicroroughness, without significant differences between the studied materials. In relation to the nanosurface topography and roughness, the reinforced PEEK material was the least modified by aging. The color changes after 4 weeks of water immersion and one year of simulated in vitro aging ranged from extremely slight to slight, for all materials. (4) Conclusions: Water absorption was associated with a decrease in microhardness. Surface characteristics are affected by water immersion and thermocycling. Perceivable or marked color changes of the materials were not detected during the study.

Considering that the processes of PEEK discoloration caused by either intrinsic or extrinsic factors require elucidation, the aim of this study was to investigate the long-term effect of the combined action of ageing and immersing solutions on the optical properties and color stability of PEEK material, related to surface processing (polishing or glazing). (2) Methods: This study aims to determine the influence of different ageing and staining protocols on optical properties, color changes, and surface roughness of a reinforced PEEK material (bioHPP, Bredent, Senden, Germany). For ageing, specimens were submitted to 5000 cycles in a 55 °C bath and a 5 °C bath filled with distilled water. For staining, thermal cycling was performed in a hot coffee bath (55 °C) and a bath filled with distilled water (37 °C) and in a cold juice bath (5 °C) and a bath filled with distilled water (37 °C). Translucency (TP) and opalescence (OP) parameters were determined, the total color change value (ΔΕ*) was calculated, specimens’ surface roughness was analyzed, and statistical analyses were performed. (3) Results: The mean TP values of the studied samples were in the interval of 1.25–3.60, which is lower than those reported for natural teeth or other aesthetic restoration materials. The OP values of PEEK were registered in the range of 0.27–0.75, being also lower than those of natural teeth or other aesthetic restoration materials. OP has a very strong positive relationship with TP. The mean registered Ra values for all subgroups were below 0.13 µm. Artificial ageing and staining in hot coffee proved to increase the roughness values. (4) Conclusions: The glazing of PEEK has a favorable effect on surface roughness and opalescence, irrespective of the artificial ageing or staining protocols. Artificial ageing damages the color stability and roughness of PEEK, regardless of surface processing, and decreases the translucency and opalescence of glazed surfaces. Immersion in hot coffee leads to perceivable discolorations.

The development of various dental glass-ceramic materials and the evolution of novel processing technologies lead to an essential change in the clinical and technical workflow. The long-term success of a dental restoration treatment is defined by its durability, which is directly influenced by the oral environment. This study’s purpose was to evaluate the artificial aging behavior of nanostructured, respective microstructured ceramics related to surface topography, roughness, and optical properties. Six monolithic restoration materials were selected: milled lithium disilicate glass-ceramic (LDS-M) MT (medium translucency), hot-pressed lithium disilicate glass-ceramic (LDS-P) MT and HT (high translucency), milled zirconia-reinforced lithium silicate ceramic (ZLS-M) MT and hot-pressed zirconia-reinforced lithium silicate ceramic (ZLS-P) MT and HT, resulting n = 96 surfaces. All the samples were artificially aged by thermal cycling, and all investigations were made before and after thermal cycling. In terms of optical properties, differences recorded between ZLS and LDS ceramics are not significant. Thermal cycling increases the translucency of ZLS and LDS glass-ceramic materials significantly, with the most harmful effect on the pressed and polished samples. Micro- and nano roughness are significantly influenced by in vitro aging and a negative correlation was recorded. Glazed samples are characterized by significant rougher surfaces for all types of materials. On nanolevel, ZLS materials are significantly smoothed by thermal cycling.