Magnetic spinel ferrite nanoparticles (MSF-NPs) are potential candidates for biomedical applications, especially in cancer diagnosis and therapy due to their excellent physiochemical and magnetic properties. In the current study, MSF-NPs were fabricated by sol-gel auto combustion method. The crystal structure and surface morphology were confirmed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The magnetic properties were studied by VSM (vibrating sample magnetometer). As increasing Gd3+ concentration, the saturation magnetization values decreased from (17.8-2.3) emu/g, while the coercivity decreased from (499-133) Oe at room temperature. Finally, the fabricated MSF-NPs were tested against anticancer activity by MTT assay. The IC50 = 21.27 μg/mL value was observed, showing the strong antiproliferative activity of these nanoparticles. These results suggested that the obtained MSF-NPs would be useful for remote-controlled hyperthermia therapy for cancer treatment and MRI application due to their excellent magnetic properties. These distinct properties make MSF-NPs most suitable for cancer treatment and bright Contrast Agents (T1-MRI).

In this research, we developed undoped and aluminum-doped zinc oxide for antimicrobial and anticancer activities. This study focuses on the synthesis, characterization, and biological activities of zinc oxide nanoparticles (ZnO NPs) and aluminum-doped zinc oxide nanocomposites (Zn_1−xAl_xO NCs) at varying concentrations (x = 0, 0.25, 0.5, and 0.75 wt%) using the coprecipitation method. Various characterization techniques such as XRD, UV-Vis, FTIR, EDX, and SEM were performed to analyze the crystal structure, optical properties, functional group identification, elemental composition, and surface morphology. The antimicrobial activity test showed that Zn_0.75Al_0.25O NCs exhibited the strongest inhibition zone against Bacillus cereus compared to Staphylococcus aureus > Pasteurella multocida > Escherichia coli. Moreover, the cytotoxicity and cell viability of liver cancer (HepG-2), breast cancer (MCF-7), ovarian cancer (SKOV3), and normal liver cell lines) were evaluated using the MTT assay, demonstrating that Zn_0.75Al_0.25O NCs not only enhance cell destruction but also show low cytotoxicity and high biocompatibility at low concentrations. These results suggest that Zn_0.75Al_0.25O NCs could be a promising candidate for in vivo anticancer applications and should be further investigated.

Silver oxide (Ag₂O) particles are wonderful candidates due to their unique properties, and their use in a wide range of research, industrial and biomedical applications is rapidly increasing. This makes it fundamental to develop simple, environmentally friendly methods with possible scaling. Herein, sodium borohydride and Datura innoxia leaf extract were applied as chemical and biological stabilizing and reducing agents to develop Ag₂O particles. The primary aim was to evaluate the anticancer and antiviral activity of Ag₂O particles prepared via two methods. XRD, UV-visible and SEM analyses were used to examine the crystallite structure, optical properties and morphology, respectively. The resulting green-synthesized Ag₂O particles exhibited small size, spherically agglomerated shape, and high anticancer and antiviral activities compared to chemically synthesized Ag₂O particles. The MTT (3-(4,5-dimethylthiazol-2-yl)-2,5 diphenyltetrazolium-bromide) assay of green-synthesized Ag₂O particles showed high anticancer activity against MCF-7 cells with IC₅₀ = 17.908 µg/mL compared to chemically synthesized Ag₂O particles with IC₅₀ = 23.856 µg/mL. The antiviral activity of green-synthesized Ag₂O particles and chemically synthesized Ag₂O particles was also evaluated by a plaque-forming assay, and green-synthesized Ag₂O particles showed higher antiviral ability with IC₅₀ = 0.618 µg/mL as compared to chemically synthesized Ag₂O particles with IC₅₀ = 6.129 µg/mL. We propose the use of green-synthesized Ag₂O particles in cancer treatment and drug delivery.

In this study, ceria nanoparticles (NPs) and deep eutectic solvent (DES) were synthesized, and the ceria-NP’s surfaces were modified by DES to form DES-ceria NP filler to develop mixed matrix membranes (MMMs). For the sake of interface engineering, MMMs of 2%, 4%, 6% and 8% filler loadings were fabricated using solution casting technique. The characterizations of SEM, FTIR and TGA of synthesized membranes were performed. SEM represented the surface and cross-sectional morphology of membranes, which indicated that the filler is uniformly dispersed in the polysulfone. FTIR was used to analyze the interaction between the filler and support, which showed there was no reaction between the polymer and DES-ceria NPs as all the peaks were consistent, and TGA provided the variation in the membrane materials with respect to temperature, which categorized all of the membranes as very stable and showed that the trend of stability increases with respect to DES-ceria NPs filler loading. For the evaluation of efficiency of the MMMs, the gas permeation was tested. The permeability of CO₂ was improved in comparison with the pristine Polysulfone (PSF) membrane and enhanced selectivities of 35.43 ($\mathsf{\alpha }$_CO2/CH4) and 39.3 ($\mathsf{\alpha }$_CO2/N2) were found. Hence, the DES-ceria NP-based MMMs proved useful in mitigating CO₂ from a gaseous mixture.

Bilayer electrospun fibers aimed to be used for skin tissue engineering applications were fabricated for enhanced cell attachment and proliferation. Different ratios of PHBV-PLLA (70:30, 80:20, and 90:10 w/w) blends were electrospun on previously formed electrospun PHBV membranes to produce their bilayers. The fabricated electrospun membranes were characterized with FTIR, which conformed to the characteristic peaks assigned for both PHBV and PLLA. The surface morphology was evaluated using SEM analysis that showed random fibers with porous morphology. The fiber diameter and pore size were measured in the range of 0.7 ± 0.1 µm and 1.9 ± 0.2 µm, respectively. The tensile properties of the bilayers were determined using an electrodynamic testing system. Bilayers had higher elongation at break (44.45%) compared to the monolayers (28.41%) and improved ultimate tensile strength (7.940 MPa) compared to the PHBV monolayer (2.450 MPa). In vitro cytotoxicity of each of the scaffolds was determined via culturing MC3T3 (pre-osteoblastic cell line) on the membranes. Proliferation was evaluated using the Alamar Blue assay on days 3, 7, and 14, respectively. SEM images of cells cultured on membranes were taken in addition to bright field imaging to visually show cell attachment. Fluorescent nuclear staining performed with DAPI was imaged with an inverted fluorescent microscope. The fabricated bilayer shows high mechanical strength as well as biocompatibility with good cell proliferation and cell attachment, showing potential for skin substitute applications.