In the final process of the bleached kraft pulp there are some cellulose fibers that are separated from the main fibers stream; these fibers are rejected and considered as a low quality fibers, these fibers are known as rejected fiber (RF). In the present work the potential use of these fibers for Cellulose Nanocrystals (CNCs) synthesis was studied. The physical and chemical properties of synthesized CNCs were characterized through different techniques such as Atomic Force Microscopy (AFM), Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD), Fourier-Transform Infrared Spectroscopy (FTIR), and Thermogravimetric Analysis (TGA). Results demonstrate the feasibility of CNCs synthesis with a yield of 28.1% and 36.9%, and crystallinity of 73.5% and 82.7%. Finally, the morphology and synthesis conditions suggest that this industrial reject fiber (RF) could be used as a source for the CNCs production, thus adding value to the kraft process and opening new possibilities for innovation in the pulp industry.

Impact of the Chemical Composition of Pinus radiata Wood on its Physical and Mechanical Properties Following Thermo-Hygromechanical Densification

Forestry industries in Chile are facing an important challenge—diversifying their products using green technologies. In this study, the potential use of Ionic Liquids (ILs) to dissolve and hydrolyze eucalyptus wood (mix of Eucalyptus nitens and Eucalyptus globulus) kraft pulp was studied. The Bleached Hardwood Kraft Pulp (BHKP) from a Chilean pulp mill was used together with five different ILs: 1-butyl-3-methylimidazolium chloride [bmim][Cl], 1-butyl-3-methylimidazolium acetate [bmim][Ac], 1-butyl-3-methylimidazolium hydrogen sulfate [bmim][HSO₄], 1-ethyl-3-methylimidazolium chloride [emim][Cl], 1-ethyl-3-methylimidazolium acetate [emim][Ac]. Experimentally, one vacuum reactor was designed to study the dissolution/hydrolysis process for each ILs; particularly, the cellulose dissolution process using [bmim][Cl] was studied proposing one molecular dynamic model. Experimental characterization using Atomic Force Microscopy, conductometric titration, among other techniques suggest that all ILs are capable of cellulose dissolution at different levels; in some cases, the dissolution evolved to partial hydrolysis appearing cellulose nanocrystals (CNC) in the form of spherical aggregates with a diameter of 40–120 nm. Molecular dynamics simulations showed that the [bmim][Cl] anions tend to interact actively with cellulose sites and water molecules in the dissolution process. The results showed the potential of some ILs to dissolve/hydrolyze the cellulose from Chilean Eucalyptus, maintaining reactive forms.

Radiata pine is the main wood species used in the Chilean construction industry, but it must be protected due to its low natural durability. Chemical protection of wood by impregnation allows for a more efficient utilization of the forest resources by extending its useful life. The use of nanoparticles in wood protection has garnered great interest during the last decade, due to their unique physicochemical properties, different from those of larger sized materials. In this research, the impregnation of radiata pine wood with copper nanoparticles (CuNP) was studied in terms of retention, penetration, leaching, and its protective effect against wood rot fungi growth according to EN 113, AWPA A3-91, A9-18, and E11-16. Penetration analysis confirmed a uniform distribution across the wood, with total penetration in the impregnated samples with the highest concentration solution of CuNP. Retention values of the impregnated wood increased proportionally with the concentration of nanoparticles evaluated by EDXRF. Leaching analysis showed copper removal during the first hours of the test, with a constant leaching rate up to 144 h. Impregnated wood mass loss (ML) due to exposure to Gloeophyllum trabeum and Rhodonia placenta fungi were significantly reduced regardless of the CuNP concentration or fungi tested, with an ML smaller than 5% and smaller than 14% for leached samples.

Kraft pulp cellulose was hydrolyzed using sulfuric acid, under different thermophysical conditions of temperature, time, pulp concentration, and sonication time. The experimental design revealed the effect of these conditions and their interaction on the hydrolysis yield obtained. In addition, the top five cellulose nanocrystals (CNCs) yields from this experiment design were analyzed. The results obtained indicated that CNCs possess a morphology that can be described as individualized rod particles, with average diameters less than 50 nm and different size distribution. In the analysis of CNCs features, significant Pearson correlations were established between the crystallinity of the CNC, CNC yield, and interplanar crystallites distance (Δd/d). The thermogravimetric (DTG) profiles exhibited two CNCs degradation stages, where the second stage CNCs degradation showed a significative correlation with CNC sulfur content. In our analysis, the crystallographic parameters exhibited a correlation with the mechanical behavior of the CNC, since the potential variation between the distances of the crystalline planes is related to the stress and deformation present in the crystallites of CNCs. This study provides new knowledge regarding CNCs, further enhancing information for CNC-based industries and the processability of CNCs for the development of new materials.

As galactoglucomananas são as principais frações de hemiceluloses presentes nas madeiras moles e contêm, principalmente, as hexoses galactose, glicose e manose. O isolamento eficiente e seletivo dessas hemiceluloses é um obstáculo crítico a superar para sua utilização. Os objetivos deste trabalho foram extrair e caracterizar soluções aquosas ácidas e neutras de hemiceluloses de cavacos de madeira de Pinus radiata, bem como avaliar sua viabilidade para a produção de bioetanol. As hemiceluloses em P. radiata representam 26 g/100 g de madeira (base seca), e as hexoses são responsáveis por aproximadamente 64% dessa quantidade. De acordo com as diferentes condições de extração, cerca de 50% da fração hemicelulósica foi solubilizada e recuperada depois de uma precipitação com etanol. As frações recuperadas de hemiceluloses estavam na forma de oligômeros com peso molecular médio (Mw) variando entre 4x10³ e 4x10(5) g/mol. Os oligômeros hemicelulósicos foram hidrolisados com ácido sulfúrico diluído e os hidrolisados concentrados até aproximadamente 70 g/L hexosas e fermentados pela levedura Saccharomyces cerevisiae. Os resultados de fermentação indicaram que os açúcares obtidos dos extratos ácidos e neutros foram fermentados com rendimentos máximos de etanol de 63% e 54% (22 g/L e 19 g/L), respectivamente. A conversão de hemiceluloses da madeira em etanol é viável, porém seu baixo rendimento faz que o processo não seja economicamente atrativo, razão por que melhorias no processo ou usos alternativos das hemiceluloses devem ser avaliados.