Applications of Carbon Fibre Reinforced Polymers (CFRP) at temperatures over 150–200 °C are becoming common in aerospace and automotive applications. Exposure of CFRP to these temperatures can lead to permanent changes in their mechanical properties. In this work, we investigated the effect of thermal ageing in air on the strength of carbon fabric/epoxy composites. To this end, accelerated artificial ageing at different temperatures was performed on carbon fabric/epoxy specimens. The flexural and interlaminar shear strengths of the aged specimens were assessed by three-point bending and short beam shear tests, respectively, and compared to those of unaged samples. For ageing at temperatures below the glass transition temperature of the resin, $T_g$, a moderate reduction of strength was found, with a maximum decrease of 25% for 2160 h at 75% $T_g$. On the other hand, a rapid strength decrease was observed for ageing temperatures above $T_g$. This was attributed to degradation of the epoxy matrix and of the fibre/epoxy interface. In particular, a 30% strength decrease was found for less than 6 h at 145% $T_g$. Therefore, it was concluded that even a short exposure to operating temperatures above $T_g$ could substantially impair the load-carrying capability of CFRP components.

Crashworthiness is a critical property that enables aerospace structures to minimise injuries and equipment damage during impact scenarios. This review examines the current state of crashworthiness research, with a focus on regulatory frameworks, experimental testing, and numerical modelling techniques. Stringent safety standards set by the Federal Aviation Administration (FAA) and the European Union Aviation Safety Agency (EASA) guide the design and certification protocols for aeronautical structures. Experimental crash testing, which includes both full-scale and subscale impact tests, provides essential data for validating material behaviour and energy absorption capabilities under both quasi-static and dynamic loading conditions. Advanced numerical modelling tools offer significant insights into crash behaviour, enabling optimisation of structural designs whilst reducing reliance on costly physical testing. This review highlights the integration of regulations, empirical data, and computational tools in advancing crashworthiness research, with an emphasis on developing safer, more efficient, and sustainable aerospace designs. Future directions should prioritise the use of sustainable materials and optimise crashworthy designs through artificial intelligence (AI) and advanced numerical models to enhance structural performance and safety.

Composite materials usage in several industrial fields is now widespread, and this leads to the necessity of overcoming issues that are still currently open. In the aeronautic industry, this is especially true for Barely Visible Impact Damage (BVID) and humidity uptake issues. BVID is the most insidious kind of impact damage, being rather common and not easily detectable. These, along with the ageing that a composite structure could face during its operative life, could be a cause of fatal failures. In this paper, the influence of water absorption on impacted specimens compressive residual strength was studied. Specimens were impacted using a modified Charpy pendulum. Two different locations were chosen for comparison: Near-Edge (NE) and Central (CI). Accelerated hygrothermal ageing was conducted on impacted and reference nonimpacted coupons, placing them in a water-filled jar at 70 °C. Compressive tests were performed in accordance with the Combined Loading Compression (CLC) test method. A Dynamic Mechanical Analysis (DMA) was performed as well. The results showed the influence of hygrothermal ageing, as expected. Nevertheless, the influence of impact location on compressive residual strength is not clearly noticeable in aged specimens, leading to the conclusion that hygrothermal ageing may have a greater effect on composite compressive strength than the analysed BVI damage.

Resin transfer molding (RTM) technologies are widely used in automotive, marine, and aerospace applications. The need to evaluate the impact of design and production critical choices, also in terms of final costs, leads to the wider use of numerical simulation in the preliminary phase of component development. The main issue for accurate RTM analysis is the reliable characterization of the involved materials. The aim of this paper is to present a validated methodology for material characterization to be implemented and introduce data elaboration in the ESI PAM-RTM software. Experimental campaigns for reinforcement permeabilities and resin viscosity measurement are presented and discussed. Finally, the obtained data are implemented in the software and then compared to experimental results in order to validate the described methodology.

Adhesively bonded joints are essential in the aeronautical industry, offering benefits such as weight reduction and enhanced sustainability. However, certifying these joints is challenging due to unreliable methods for assessing their strength and the development of predictive models for fatigue-driven disbonding remains an ongoing effort. This manuscript presents the implementation and validation of a cohesive zone model for studying high-cycle fatigue disbonding under Mode I and Mixed-Mode loading. The model was integrated into the commercial finite element analysis software Abaqus using user-defined material subroutine (UMAT). Two modelling approaches were investigated: one replacing the adhesive with a cohesive layer, and the other incorporating a cohesive layer at the adhesive’s mid-plane while modelling its entire thickness, using both 2D and 3D techniques. Validation was conducted against experimental data from the literature that examined the influence of adhesive thickness on fatigue behaviour in DCB and CLS tests. The findings of this study confirm that the model accurately predicts fatigue disbonding across all cases examined. Additionally, the analysis reveals that modelling adhesive thickness plays a critical role in the simulation’s outcomes. Variations in adhesive thickness can significantly alter the crack growth behaviour, highlighting the importance of carefully considering this parameter in future assessments and applications.