The post-synthesis procedure for cyclic amine (morpholine and 1-methylpiperazine) modified mesoporous MCM-48 and SBA-15 silicas was developed. The procedure for preparation of the modified mesoporous materials does not affect the structural characteristics of the initial mesoporous silicas strongly. The initial and modified materials were characterized by XRD, N₂ physisorption, thermal analysis, and solid-state NMR. The CO₂ adsorption of the obtained materials was tested under dynamic and equilibrium conditions. The NMR data revealed the formation of different CO₂ adsorbed forms. The materials exhibited high CO₂ absorption capacity lying above the benchmark value of 2 mmol/g and stretching out to the outstanding 4.4 mmol/g in the case of 1-methylpiperazin modified MCM-48. The materials are reusable, and their CO₂ adsorption capacities are slightly lower in three adsorption/desorption cycles.

Nanogels (NGs) have attracted great attention because of their outstanding biocompatibility, biodegradability, very low toxicity, flexibility, and softness. NGs are characterized with a low and nonspecific interaction with blood proteins, meaning that they do not induce any immunological responses in the body. Due to these properties, NGs are considered promising candidates for pharmaceutical and biomedical application. In this work, we introduce the development of novel functional nanogel obtained from two naturally based products—citric acid (CA) and pentane-1,2,5-triol (PT). The nanogel was synthesized by precipitation esterification reaction of CA and PT in tetrahydrofuran using N-ethyl-N′-(3-dimethylaminopropyl) carbodiimide (EDC) and 4-(dimethylamino)pyridine (DMAP) catalyst system. Dynamic light scattering (DLS), cryogenic transmission electron microscopy (cryo-TEM) and atomic force microscopy (AFM) analyses revealed formation of spherical nanogel particles with a negative surface charge. Next, the nanogel was loaded with doxorubicin hydrochloride (DOX) by electrostatic interactions between carboxylic groups present in the nanogel and amino groups of DOX. The drug-loaded nanogel exhibited high encapsulation efficiency (EE~95%), and a bi-phasic release behavior. Embedding DOX into nanogel also stabilized the drug against photodegradation. The degradability of nanogel under acidic and neutral conditions with time was investigated as well.

Hydrogels are superior wound dressings because they can provide protection and hydration of the wound, as well as the controlled release of therapeutic substances to aid tissue regeneration and the healing process. Hydrogels obtained from natural precursors are preferred because of their low cost, biocompatibility, and biodegradability. We describe the synthesis of novel functional hydrogels based on two natural products—citric acid (CA) and pentane-1,2,5-triol (PT, a product from lignocellulose processing) and poly(ethylene glycol) (PEG-600)—via an environment friendly approach. The hydrogels were prepared via monomer crosslinking through a polycondensation reaction at an elevated temperature in the absence of any solvent. The reagents were blended at three different compositions with molar ratios of hydroxyl (from PT and PEG) to carboxyl (from CA) groups of 1:1, 1:1.4, and 1.4:1, respectively. The effect of the composition on the physicomechanical properties of materials was investigated. All hydrogels exhibited pH-sensitive behavior, while the swelling degree and elastic modulus were dependent on the composition of the polymer network. The proteolytic enzyme serratiopeptidase (SER) was loaded into a hydrogel via physical absorption as a model drug. The release profile of SER and the effects of the enzyme on healthy skin cells were assessed. The results showed that the hydrogel carrier could provide the complete release of the loaded enzyme.