The last few decades have seen rapid growth in additive manufacturing (AM) technologies. AM has implemented a novel method of production in design, manufacture, and delivery to end-users. Accordingly, AM technologies have given great flexibility in design for building complex components, highly customized products, effective waste minimization, high material variety, and sustainable products. This review paper addresses the evolution of engineering design to take advantage of the opportunities provided by AM and its applications. It discusses issues related to the design of cellular and support structures, build orientation, part consolidation and assembly, materials, part complexity, and product sustainability.

Triply periodic minimum surface (TPMS)-based lattice structures have gained interest for their outstanding capacity to absorb energy, their high load-bearing capacity, and their high surface-to-volume ratio. This study considered three TPMS cell topologies, including Diamond, Gyroid, and Primitive. The FDM process was used to print the lattice structures with two materials: pure polylactic acid (PLA) and carbon fiber-reinforced PLA (PLA + CF). The influence of carbon fiber (CF) incorporation, unit cell type (topologies) and size, and relative density (RD) on mechanical properties and failure patterns were explored comprehensively under uniaxial compression testing. The results demonstrate a change in the compressive modulus (0.09 to 0.47 GPa), compressive strength (2.98 to 13.89 MPa), and specific energy absorption (SEA) (0.14 MJ/m³/g to 0.58 MJ/m³/g) due to the influence of CF incorporation, cell type and size, and RD. Results indicate that the Diamond structure outperformed both Primitive and Gyroid structures in terms of compressive modulus and strength, and SEA. All the CF-based TPMS structures showed a higher compressive modulus. Compressive strength and energy absorption capacity were both slightly enhanced in most PLA + CF-based Diamond structures. On the contrary, Gyroid and Primitive structures showed better performance for pure PLA-based structures in terms of compression strength and specific absorption energy.

The emerging demands of industry for developing the novel materials with superior mechanical properties have successfully resulted in the development of distinct materials such as Al-matrix composites. Among these composites, newly developed Al6061-7.5% SiC holds promising mechanical characteristics. But, the SiC reinforcement in the Al-matrix makes the machining of this composite challenging, thus posing a serious concern regarding its effective utilization. In this research, high-speed wire electric discharge machining (WEDM) was employed for the precise machining of a squeeze casted Al6061-7.5% SiC composite. The cutting performance of the WEDM was assessed in terms of roughness (S_R), cutting rate (C_s) and kerf width (K_W). Experimentation was performed according to the response surface methodology. The experimental findings were thoroughly investigated using statistical, optical and scanning electron microscopic (SEM) analyses. It has been revealed that the voltage is most influential/contributing parameter (having a percentage contribution of 25%) for controlling theS_Rduring WEDM of Al6061-7.5% SiC composite, whereas for theC_SandK_W, pulse and current are the major contributing control variables with percentage contributions of 90% and 84%, respectively. At low magnitude of both current and voltages, the surface quality is improved up to 33.3%. The SEM and optical microscopic evidences reveal shallow craters, small size melt re-deposits and micro globules on the machined surface at lower settings of both the said variables. Contrarily, for achieving higher cutting speed, high values of current and voltage along with low pulse are deemed essential. In case ofK_W, low magnitude of current and voltage along with smaller pulse yields 20% reduction in the kerf width. The analyses revealed the conflicting nature of the studied output responses (S_R,C_sandK_W). Therefore, multi-objective genetic algorithm (MOGA) was used to find a parametric combination. The best combination of WEDM input parameters found is current = 3 A, voltage = 84.999 V and pulse = 10 mu. This combination gives a minimumS_Rof 5.775 μm with aK_Wof 0.3111 mm at aC_Sof 5.885 mm/min. The suitability of the MOGA-proposed parametric combination was witnessed through confirmation trials. Furthermore, the parametric effects have also been mathematically quantified with respect to the defined machinability parameters.

Titanium alloys, especially Ti-6Al-4V, which is considered a difficult-to-cut material, bears numerous applications in aerospace and biomedical sectors. The criticality of the accurate formation of the machined cavity for the said applications and properties of Ti-6Al-4V accentuated the use of electric discharge machining (EDM). However, the issues of lower material removal rate (MRR) and tool wear (TWR) discouraged the use of EDM. These inherent issues hold a pivotal role regarding the sustainable machining of Ti-alloy. Therefore, in this research the potentiality of kerosene-based dielectric, having graphene nanoparticles, is comprehensively examined for the sustainable EDM of Ti-6Al-4V, which was not focused upon yet. Experimentation was performed under Taguchi’s design (L18) with three types of electrodes, namely Aluminum, Brass and Copper. In total, 36 experiments were conducted, of which 18 were with graphene-mixed dielectric and the remaining were with kerosene. Experimental results reveal that the brass electrode with negative tool polarity yields higher MRR for both types of dielectrics. The maximum MRR (7.602 mm³/min) achieved with graphene mixed dielectric is 64.5% greater as compared to that obtained with kerosene (4.621 mm³/min). Moreover, the minimum TWR obtained for graphene-based dielectric, i.e., 0.17 mg/min is approximately 1.5 times less than that achieved with kerosene.