Concentration, gel strength (Bloom), and pH effects on both melting and gelling temperatures of gelatin were studied using small amplitude oscillatory rheology. Temperature sweeps were applied to gelatin gel samples for heating and cooling at fixed frequencies. Results showed that melting temperatures were higher than gelling temperatures, and both increased with increasing concentration at pH from 3 to 6 for all gel strength. For constant gelatin concentration and pH, as gel strength increased, melting temperatures decreased, whereas gelling temperatures increased. A mathematical model was obtained which correlates melting and gelling temperatures, respectively, with pH and concentration at fixed Bloom degrees. All gelatin gels showed storage modulus higher (2 to 10 kPa) than loss modulus (50 to 500 Pa).

Encapsulated fat-soluble powders containing vitamin A (VA) and E (VE) were prepared as a feasible additive for extruded feed products. The effect of the encapsulating agents (Capsul-CAP^®, sodium caseinate-SC) in combination with Tween 80 (TW) as an emulsifier and maltodextrin (MD) as a wall material on the physicochemical properties of emulsions and powders was evaluated. First, nanoemulsions containing MD:CAP:TW:VA/VE and MD:SC:TW:VA/VE were prepared and characterized. Then, powders were obtained by means of spray-drying and analyzed in terms of the product yield, encapsulation efficiency, moisture content, porosity, surface morphology, chemical structure, and thermal properties and thermo-oxidative/thermal stability. Results showed that although nanoemulsions were obtained for all the compositions, homogeneous microcapsules were found after the drying process. High product yield and encapsulation efficiency were obtained, and the presence of the vitamins was corroborated. The characteristics of the powders were mainly influenced by the encapsulating agent used and also by the type of vitamin. In general, the microcapsules remained thermally stable up to 170 °C and, therefore, the proposed encapsulation systems for vitamins A and E were suitable for the preparation of additives for the feed manufacturing through the extrusion process.