Water pollution is one of the most serious problems worldwide. Nanocellulose-based aerogels usually show excellent adsorption capacities due to their high aspect ratio, specific surface area and surface charge, making them ideal for water purification. In this work, (ligno)cellulose nanofibers (LCNFs/CNFs) from wheat straw residues were obtained using two types of pre-treatments: mechanical (Mec) and TEMPO-mediated oxidization (TO), to obtain different consistency (0.2, 0.4, 0.6 and 0.8) bioaerogels, and their adsorption capacities as dye removers were further studied. The materials were characterized in terms of density, porosity and mechanical properties. An inversely proportional relationship was observed between the consistencies of the aerogels and their achieved densities. Despite the increase in density, all samples showed porosities above 99%. In terms of mechanical properties, the best results were obtained for the 0.8% consistency LCNF and CNF-Mec aerogels, reaching 67.87 kPa and 64.6 kPa for tensile strength and Young’s modulus, respectively. In contrast, the adsorption capacity of the aerogels was better for TEMPO-oxidized aerogels, reaching removal rates of almost 100% for the CNF-TO5 samples. Furthermore, the residual lignin content in LCNF-Mec aerogels showed a great improvement in the removal capacity, reaching rates higher than 80%, further improving the cost efficiency of the samples due to the reduction in chemical treatments.

The growing demand for plant fiber-reinforced composites offers new opportunities to compete against glass fiber (GF)-reinforced composites, but their performance must be assessed, revised, and improved as much as possible. This work reports on the production and the flexural strength of composites from polypropylene (PP) and hemp strands (20–50 wt.%), using maleic anhydride-grafted PP (MAPP) as a compatibilizer. A computational assessment of the reaction between cellulose and MAPP suggested the formation of only one ester bond per maleic anhydride unit as the most stable product. We determined the most favorable MAPP dosage to be 0.06 g per gram of fiber. The maximum enhancement in flexural strength that was attained with this proportion of MAPP was 148%, corresponding to the maximum fiber load. The modified rule of mixtures and the assumption of similar coupling factors for tensile and flexural strength allowed us to estimate the intrinsic flexural strength of hemp strands as 953 ± 116 MPa. While falling short of the values for sized GF (2415 MPa), the reinforcement efficiency parameter of the natural fibers (0.209) was found to be higher than that of GF (0.045).

An innovative colloidal approach is proposed here to carry out the customized functionalization of TEMPO-Oxidized Cellulose Nanofibers (CNF) incorporating non-noble inorganic nanoparticles. A heterocoagulation process is applied between the delignified CNF and as-synthetized CuO nanoparticles (CuO NPs) to formulate mixtures which are used in the preparation of aerogels with antibacterial effect, which could be used to manufacture membranes, filters, foams, etc. The involved components of formulated blending, CNF and CuO NPs, were individually obtained by using a biorefinery strategy for agricultural waste valorization, together with an optimized chemical precipitation, assisted by ultrasounds. The optimization of synthesis parameters for CuO NPs has avoided the presence of undesirable species, which usually requires later thermal treatment with associated costs. The aerogels-based structure, obtained by conventional freeze-drying, acted as 3D support for CuO NPs, providing a good dispersion within the cross-linked structure of the nanocellulose and facilitating direct contact of the antibacterial phase against undesirable microorganisms. All samples showed a positive response against Escherichia coli and Staphylococcus aureus. An increase of the antibacterial response of the aerogels, measured by agar disk diffusion test, has been observed with the increase of CuO NPs incorporated, obtaining the width of the antimicrobial “halo” (nw_halo) from 0 to 0.6 and 0.35 for S. aureus and E. coli, respectively. Furthermore, the aerogels have been able to deactivate S. aureus and E. coli in less than 5 h when the antibacterial assays have been analyzed by a broth dilution method. From CNF-50CuO samples, an overlap in the nanoparticle effect produced a decrease of the antimicrobial kinetic.

Conventional Pickering emulsions (PEs) stabilizers are often petrochemical-based, raising concerns about bioincompatibility and adverse reactions. Using sustainable biomass, such as pruning residues, offers potential for natural PEs stabilizers development. This study explores the use of avocado pruning lignin (APL), alongside various commercial lignins, to produce natural stabilizers for neutral-pH PE. The effect of lignin chemical and structural composition to produce lignin nanoparticles (NP) and microparticles (MP) was studied. APL exhibited high carbohydrate content, contributing to excellent surface tension reduction and enhanced antimicrobial properties. However the presence of carbohydrates compromised APL solubility in acetone:water mixtures, hindering the nanoprecipitation process via the solvent exchange method. A washing step, consisting in the removal of water-soluble fraction of APL (APLWEF) improved this process. Both lignin NPs and MPs demonstrated effective stabilization of neutral-pH PEs, maintaining stability for up to 27 days with minimal changes in creaming index (CI). Quercetin encapsulation efficiency (EE) in all lignin types exceeded 90 %, except for APLWEF, which showed an EE around 78 %. The antioxidant activity in emulsions incorporating quercetin was particularly high, with kraft lignin sample maintaining an activity level of 0.93 mg of Trolox equivalents per g of emulsion at day 10, exhibiting minimal change from day 0.