ZnO homo-structures with tunable photoluminescence and band gap.

The transmission electron microscope electron-beam (TEM e-beam) as a material modification tool has been demonstrated. The material modification is realised in the high-resolution TEM mode (largest condenser aperture, 150 μm, and 200 nm spot size) at a 200 keV beam energy. The Cu₂(OH)₃NO₃ (CHN) nanoflakes used in this study were microwave solution processed that were layered single crystals and radiation sensitive. The single domain CHN flakes disintegrate into a large number of individual CuO crystallites within a 90 s span of time. The sequential bright-field, dark-field, and selected area electron diffraction modes were employed to record the evolved morphology, microstructural changes, and structural transformation that validate CHN modification. High-resolution transmission electron microscopy imaging of e-beam irradiated regions unambiguously supports the growth of CuO nanoparticles (11.8(3.2) nm in diameter). This study demonstrates e-beam irradiation induced CHN depletion, subsequent nucleation and growth of nanocrystalline CuO regions well embedded in the parent burnt porous matrix which can be useful for miniaturized sensing applications. NaBH₄ induced room temperature reduction of CHN to elemental Cu and its printability on paper was also demonstrated.

Isolation and stabilization of Al nanoparticles has been possible by the room temperature reaction between SiCl₄ and LiAlH₄ in the presence of poly(vinylpyrrolidone) (PVP) under sonication. The present investigation explained that the Al from LiAlH₄ produced Al nanoparticles while SiCl₄ was converted to hydrosilanes. The formation of Al nanoparticles from this reaction was established by thorough characterization using PXRD patterns, ²⁷Al MAS-NMR spectra and HRTEM micrographs. The isolation of Al nanoparticles from this reaction clearly explained the products formed in this reaction.

We report for the first time on the antimicrobial activity of MgB₂ powders produced via the Reactive Liquid Infiltration (RLI) process. Samples with MgB₂ wt.% ranging from 2% to 99% were obtained and characterized, observing different levels of grain aggregation and of impurity phases. Their antimicrobial activity was tested against Staphylococcus aureus ATCC BAA 1026, Enterococcus faecalis ATCC 29212, Escherichia coli ATCC 25922, Pseudomonas aeruginosa ATCC 27853, and Candida albicans ATCC 10231. A general correlation is observed between the antibacterial activity and the MgB₂ wt.%, but the sample microstructure also appears to be very important. RLI-MgB₂ powders show better performances compared to commercial powders against microbial strains in the planktonic form, and their activity against biofilms is also very similar.