One of the most common loading conditions that bonded joints experience in service is repeated impact. Despite the destructive effects of impact fatigue, the behavior of metal-composite bonded joints subjected to repeated impact loads has rarely been studied in the literature. Therefore, it is of utmost importance to pay attention to this phenomenon on the one hand and to find solutions to improve the impact fatigue life of bonded composite metal components on the other hand. Accordingly, in this study, the use of the bi-adhesive technique is proposed to improve the durability of composite-metal single-lap joints (SLJs) under impact fatigue loading conditions. J-N (energy-life) method is also used to analyze the experimental data obtained. Accordingly, in the present study, the impact fatigue behavior of single adhesive metal to composite joints was analyzed experimentally based on the J-N method and also numerically using the finite element method (FEM). By using two adhesives along a single overlap, the impact fatigue life of joints between dissimilar composite and metal joints was also analyzed experimentally. The results show that the double adhesives technique can significantly improve the impact fatigue life of the tested joints. It was also found that the optimum length ratio of the adhesives (the length covered by the ductile adhesive relative to the total overlap size) is a function of the stiffness of the joint and is more pronounced for less stiff bonded joints. A linear elastic numerical analysis was also conducted to evaluate the stress state along the bloodline of the bonded joints. Results show that the compressive peel stress made at the boundary of the two adhesives can be a possible reason behind the different results observed.

In contemporary engineering practices, the utilization of sustainable materials and eco-friendly techniques has gained significant importance. Wooden joints, particularly those created with polyurethan-based bio-adhesives, have garnered significant attention owing to their intrinsic environmental advantages and desirable mechanical properties. In comparison to conventional joining methods, adhesive joints offer distinct benefits such as an enhanced load distribution, reduced stress concentration, and improved aesthetic appeal. In this study, reference and toughened single-lap joint samples were investigated experimentally and numerically under quasi-static loading conditions. The proposed research methodology involves the infusion of a bio-adhesive into the wooden substrate, reinforcing the matrix of its surfaces. This innovative approach was developed to explore a synergetic effect of both wood and bio-adhesive. The experimentally validated results showcase a significant enhancement in joint strength, demonstrating an 85% increase when compared to joints with regular pine substrates. Moreover, the increased delamination thickness observed in toughened joints was found to increase the energy absorption of the joint.

In modern engineering applications, the use of sustainable materials and eco-friendly methods has become increasingly important. Wood joints, especially those strengthened with bio-adhesive, have attracted considerable attention due to their inherent environmental benefits and desirable mechanical properties. Compared to traditional joining methods, adhesive joints offer unique advantages such as improved load distribution, reduced stress concentration, and enhanced aesthetic appeal. This study aims to enhance delamination resistance in wooden adhesive joints using a novel method involving reinforced high-toughness resin on surfaces. Additionally, a hybrid substrate approach applies a tough layer to outer plies and a densified wood core with greater fiber direction strength. Normal, toughened, and hybrid single-lap joint specimens were analyzed through both experimental and numerical methods under various loading conditions, including quasi-static and intermediate rates. The proposed method involved bio-adhesive penetration into the wood substrate, forming a reinforced surface zone. The experimentally validated results show a significant improvement in joint strength, exhibiting an approximate 2.8-fold increase for the toughened joints compared to the reference joints under intermediate-rate conditions. Furthermore, the absorbed energy of the toughened joints increased by a substantial factor of up to 4.5 times under the same conditions. The fracture surfaces analysis revealed that the toughening method changed the failure mechanism of the joints from delamination to fiber breakage, indicating that the strength of the substrate was lower than that of the joint under impact conditions. The viscoelastic behavior of the bio-adhesive also influenced the response of the joints to the changing displacement rate. The toughening method enhanced the resilience and load-bearing capacity of the wood joints, making them more suitable for dynamic applications.