Secondary aluminum dross is a byproduct of the electrolytic aluminum industry, whose main components are Al₂O₃, AlN and Na₃AlF₆. Secondary aluminum dross is a type of hazardous waste, with a tremendous yield every year. Realizing the harmless treatment or resource utilization of secondary aluminum dross has important economic and social benefits. In the present research, the process of preparing premelted calcium aluminate slag used for molten steel refining from secondary aluminum dross was studied in detail. Firstly, the chemical composition and phase component of secondary aluminum dross were analyzed systematically. Then, according to phase diagram analysis and melting point measurement, the appropriate mixing ratio of CaO and secondary aluminum dross and the appropriate calcination temperature were determined. On this basis, an experiment of premelted calcium aluminate slag preparation was carried out in a tubular resistance furnace. The phase component and micromorphology of the premelted slag were analyzed by XRD and SEM. The results show that the main component of the premelted calcium aluminate slag is 11CaO·7Al₂O₃·CaF₂ phase with a low melting point. The original Na₃AlF₆ phase, which is the cause of leachable fluoride in secondary aluminum dross, disappears totally, and there is no water-soluble fluoride detected in the leaching toxicity detection. The research indicates that the process of preparing premelted calcium slag from secondary aluminum dross is feasible, which provides a helpful reference for the resource utilization of secondary aluminum dross.