Titanium and its alloys are reference materials in biomedical applications because of their desirable properties. However, one of the most important concerns in long-term prostheses is bone resorption as a result of the stress-shielding phenomena. Development of porous titanium for implants with a low Young’s modulus has accomplished increasing scientific and technological attention. The aim of this study is to evaluate the viability, industrial implementation and potential technology transfer of different powder-metallurgy techniques to obtain porous titanium with stiffness values similar to that exhibited by cortical bone. Porous samples of commercial pure titanium grade-4 were obtained by following both conventional powder metallurgy (PM) and space-holder technique. The conventional PM frontier (Loose-Sintering) was evaluated. Additionally, the technical feasibility of two different space holders (NH₄HCO₃ and NaCl) was investigated. The microstructural and mechanical properties were assessed. Furthermore, the mechanical properties of titanium porous structures with porosities of 40% were studied by Finite Element Method (FEM) and compared with the experimental results. Some important findings are: (i) the optimal parameters for processing routes used to obtain low Young’s modulus values, retaining suitable mechanical strength; (ii) better mechanical response was obtained by using NH₄HCO₃ as space holder; and (iii) Ti matrix hardening when the interconnected porosity was 36–45% of total porosity. Finally, the advantages and limitations of the PM techniques employed, towards an industrial implementation, were discussed.

A great variety of powder metallurgy techniques can produce biomimetic porous titanium structures with similar mechanical properties to host bone tissue. In this work, loose sintering and space holder techniques, two frequently used metallurgical techniques, are compared to evaluate the influences of porosity (content, size, morphology and wall roughness), mechanical properties (stiffness and yield strength) and in-vitro cellular responses (adhesion and proliferation of myoblasts and osteoblasts). These comparisons are made to achieve the best balance between biomechanical and bifunctional behavior of a partial porous implant for cortical bone replacement. Cell adhesion (filopodia presence) and spreading were promoted on both porous surfaces and fully dense substrates (non-porous control surfaces). Porous scaffold samples designed using 50 vol.% NaCl space holder technique had an improved bioactive response over those obtained with the loose sintering technique due to higher roughness and scaffold pore diameter. However, the presence of large and heterogeneous pores compromises the mechanical reliability of the implant. Considering both scenarios, the substrates obtained with 40 vol.% NH₄HCO₃ and pore size ranges between 100 and 200 μm provide a balanced optimization of size and strength to promote in-vitro osseointegration.