Gas sensing is of significant importance in a wide range of disciplines, including industrial safety and environmental monitoring. In this work, a low-cost SILAR (Successive Ionic Layer Adsorption and Reaction) technique was employed to fabricate pure CuO, Zn-doped CuO, and Na-doped CuO nanotextured films to efficiently detect CO₂ gas. The structures, morphologies, chemical composition, and optical properties of all films are characterized using different tools. All films exhibit a crystalline monoclinic phase (tenorite) structure. The average crystallite size of pure CuO was 83.5 nm, whereas the values for CuO/Zn and CuO/Na were 73.15 nm and 63.08 nm, respectively. Subsequently, the gas-sensing capabilities of these films were evaluated for the detection of CO₂ in terms of sensor response, selectivity, recovery time, response time, and limits of detection and quantification. The CuO/Na film offered the most pronounced sensitivity towards CO₂ gas, as evidenced by a sensor response of 12.8% at room temperature and a low limit of detection (LoD) of 2.36 SCCM. The response of this sensor increased to 64.5% as the operating temperature increased to 150 °C. This study thus revealed a brand-new CuO/Na nanostructured film as a highly effective and economically viable sensor for the detection of CO₂.

In this work, a low-cost, high-yield hydrothermal treatment was used to produce nanozeolite (Zeo), nanoserpentine (Serp), and Zeo/Serp nanocomposites with weight ratios of 1:1 and 2:1. At 250 °C for six hours, the hydrothermal treatment was conducted. Various methods are used to explore the morphologies, structures, compositions, and optical characteristics of the generated nanostructures. The morphological study revealed structures made of nanofibers, nanorods, and hybrid nanofibril/nanorods. The structural study showed clinoptilolite monoclinic zeolite and antigorite monoclinic serpentine with traces of talcum mineral and carbonates. As a novel photoelectrochemical catalyst, the performance of the Zeo/Serp (2:1) composite was evaluated for solar hydrogen generation from water splitting relative to its constituents. At −1 V, the Zeo/Serp (2:1) composite produced a maximum current density of 8.44 mA/g versus 7.01, 6.74, and 6.6 mA/g for hydrothermally treated Zeo/Serp (1:1), Zeo, and Serp, respectively. The Zeo/Serp (2:1) photocatalysts had a solar-to-hydrogen conversion efficiency (STH) of 6.5% and an estimated hydrogen output rate of 14.43 mmole/h.g. Consequently, the current research paved the way for low-cost photoelectrochemical catalytic material for efficient solar hydrogen production by water splitting.