Metastable β-type Ti alloys with non-toxic addition elements such as Mo, Zr, Sn, Ta and Nb were developed as an alternative to the widely used Ti-6Al-4V alloy for biomedical applications. These alloys possess enhanced biocompatibility and reduced elastic modulus in comparison with Ti-6Al-4V. Moreover, for orthopedic implants, low Young's modulus is required in order to avoid the stress shielding phenomenon. This study analyzes the microstructure and mechanical properties of a new Ti-12Mo-8Nb alloy after hot swaging, annealing at 950 ºC for 1h and water quenching. The alloy was characterized by X-ray diffraction, optical microscopy and transmission electron microscopy. Tensile tests were performed at room temperature. Young's modulus and hardness values were also measured. The structural characterization reveals a metastable β structure containing only a small amount of α and ω phases. Exhibiting a lower Young's modulus than Ti-6Al-4V and other previously studied Ti-Mo-Nb alloys, the Ti-12Mo-8Nb alloy can be a promising alternative for orthopedic application.

Metastable β-Ti alloys have become one of the most attractive implant materials due to their high biocorrosion resistance, biocompatibility, and mechanical properties, including lower Young’s modulus values. Mechanical properties of these alloys are strongly dependent on the final microstructure, which is controlled by thermomechanical treatment processing, in particular the Young’s modulus and hardness. The aim of this work was to analyze the influence of phase precipitations in heat-treated Ti-12Mo-xNb (x = 0, 3, 8, 13, 17, and 20) alloys. The alloys were prepared via arc melting and treated at 950 °C/1 h, and then quenched in water. The microstructures were analyzed by optical microscopy, transmission electron microscopy, and X-ray diffraction. Mechanical properties were based on Vickers microhardness tests and Young’s modulus measurements. Microstructural characterization showed that α″ and ω stability is a function of Nb content for the Ti–12Mo base alloy. Nb addition resulted in the suppression of the α″ phase and decrease in the ω phase volume fraction. Although the ω phase decreased with higher Nb contents, ω particles with ellipsoidal morphology were still observed in the Ti–12Mo–20Nb alloy. The α″ phase suppression by Nb addition caused a marked increase in the Young’s modulus, which decreased back to lower values with higher Nb concentrations. On other hand, the decrease in the ω phase continuously reduced alloy hardness. The study of the effect of chemical composition in controlling the volume fraction of these phases is an important step for the development of β-Ti alloys with functional properties.

A new generation of titanium alloys with non-toxic, non-allergenic elements and lower Young’s modulus (YM) have been developed, presenting modulus values close to that of bone. In titanium alloys, the value of the Young’s modulus is strongly dependent on the chemical composition. Young’s modulus also depends on the present phases and on the crystallographic texture related to the thermomechanical processing. A lower YM is normally attributed to the formation of the α″ phase into the β matrix, but there is no consensus for this assumption. In the present work, four alloys were designed and melted, based on the Ti-Nb-Mo-Zr system and heat-treated to favor the formation of the β phase. The alloys were produced by arc melting under argon atmosphere and heat-treated at 1000 °C for 24 h under high vacuum, being subsequently quenched in water to room temperature. Alloys were then characterized by optical microscopy (OM), X-ray diffraction (XRD) and transmission electron microscopy (TEM). Young’s modulus was determined by the impulse excitation technique and Vickers microhardness. The purpose of the study was to define an optimal chemical composition for the further production on a semi-industrial scale of a new Ti-Nb-Mo-Zr alloy for orthopedic implant manufacturing. The results showed that all of the four studied alloys are potential candidates for biomedical applications. Among them, the Ti-24Nb-4Mo-6Zr alloy has the lowest Young’s modulus and the highest microhardness. So, this alloy presents the highest HV/YM ratio, which is a key indicator in order to evaluate the mechanical performance of metallic biomaterials for orthopedic implants.

Metastable β titanium alloys are developed for biomedical applications due to their low Young’s moduli and functional properties. These alloys can be fitted to different parts of orthopedic implants through thermomechanical processing and chemical composition control. This study aimed to produce, process, and characterize a new metastable β titanium Ti-23.6Nb-5.1Mo-6.7Zr alloy on a semi-industrial scale for orthopedic implant manufacturing, and to discuss the influence of the cold rolling and transformed phases during aging in the microstructure and mechanical properties. This alloy was produced in a vacuum arc remelting furnace (VAR) and thermomechanically processed under different conditions. The samples were characterized by X-ray diffractometry, optical, and scanning electron microscopy, and Young’s modulus (YM) and Vickers Hardness (HV) tests. Among other processing conditions, the sample that was 50% cold rolled after solution treatment, which resulted in a microstructure with β and α″ phases, had the lowest YM (~57 GPa), and the sample aged at 300 °C for 2 h had the highest HV/YM ratio (5.42). The new alloy produced in this work, processed by different routes, showed better mechanical properties than most recently developed metastable Ti-β Alloys.