This work investigates the structural, magnetic and magneto-optical properties of a new zinc phosphate-tellurite glass belonging to the 45ZnO-10Al₂O₃-40P₂O₅-5TeO₂ system. The glass was prepared by a wet method of processing the starting reagents followed by suitable melting–stirring–quenching–annealing steps. Specific parameters such as density, average molecular mass, molar volume, oxygen packaging density, refractive index, molar refractivity, electronic polarizability, reflection loss, optical transmission, band gap and optical basicity have been reported together with thermal, magnetic and magneto-optical characteristics. Absorption bands appear in the blue and red visible region, while over 600 nm the glass becomes more transparent. FTIR and Raman spectra evidenced phosphate-tellurite vibration modes proving the P₂O₅ and TeO₂ network forming role. Magnetic measurements reveal the diamagnetic character of the Te-doped glass with an additional weak ferromagnetic signal, specific to diluted ferromagnetic oxides. Positive Faraday rotation angle with monotonous decreasing value at increasing wavelength was evidenced from magneto-optical measurements. The final product is a composite material comprising of a non-crystalline vitreous phase and Te-based nanoclusters accompanied by oxygen vacancies. The metallic-like Te colloids are responsible for the dark reddish color of the glass whereas the accompanying oxygen vacancies might be responsible for the weak ferromagnetic signal persisting up to room temperature.

The interest in ultrathin silver (Ag) films has increased due to their high surface plasmon resonance for coatings of only a few nm. Low roughness ultrathin films of 1 to 9 nm have been deposited on different substrates, such as polyethylene terephthalate (PET) and optical glass, using radio frequency (RF) magnetron sputtering. Films show good surface plasmon resonance up to 7 nm thickness, as revealed by the ultraviolet-visible (UV-Vis) spectra. The roughness of the films, investigated by Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM), is small, and one can conclude that depositions are smooth and homogeneous. The bandgap values decrease with film thickness. The refractive index of the films, calculated from ellipsometry measurements, leads to values of under 1 visible domain, with minima in the wavelength range of 400–600 nm. The results are useful for obtaining lower roughness ultrathin Ag films with good surface plasmon resonance for photonic applications.

Vanadate glasses exhibit semiconducting property at certain temperatures. This work demonstrates the conductivity of the composition 45V₂O₅–25B₂O₃–30P₂O₅, which is a new glass in the vanadium-boron-phosphorus ternary system that expands the glass forming area reported in literature data. The glass was obtained through a classical melt-quenching technique. The structural composition of the obtained glass was revealed with Raman spectroscopy and the amorphous characteristic has been highlighted with X-ray diffraction. The characteristic temperatures and the thermal expansion coefficient were determined by dilatometry. Based on the experimental measurements of electrical resistance, mathematical calculations were performed, resulting in a conductivity of 2.04·10⁻⁶ S/cm at 125 °C, and an activation energy of 42.91 kJ/mol for this glass. Impedance spectroscopy in DC and AC at 100 V and 100 Hz to 2 MHz, respectively, showed a lower activation energy of about 0.166 eV and transition temperatures of 24 °C and 11 °C, respectively. These results were compared with those from the literature considering the temperatures at which the reported conductivities were measured. This glass has potential applications in electronic devices and temperature sensors.