Thermodynamic driving forces and growth rates in rapid solidification are analysed. Taking into account the relaxation time of the solute diffusion flux in the model equations, the present theory uses, in a first case, the deviation from local chemical equilibrium, and ergodicity breaking. The second case of ergodicity breaking may exist in crystal growth kinetics of rapidly solidifying glass-forming metals and alloys. In this case, a theoretical analysis of dendritic solidification is given for congruently melting alloys in which chemical segregation does not occur. Within this theory, a deviation from thermodynamic equilibrium is introduced for high undercoolings via gradient flow relaxation of the phase field. A comparison of the present derivations with previously verified theoretical predictions and experimental data is given. This article is part of the theme issue ‘Heterogeneous materials: metastable and non- ergodic internal structures’.

Using the phase field crystal model (PFC model), an analysis of slow and fast dynamics of solid-liquid interfaces in solidification and melting processes is presented. Dynamical regimes for cubic lattices invading metastable liquids (solidification) and liquids propagating into metastable crystals (melting) are described in terms of the evolving amplitudes of the density field. Dynamical equations are obtained for body-centered cubic (bcc) and face-centered cubic (fcc) crystal lattices in one- and two-mode approximations. A universal form of the amplitude equations is obtained for the three-dimensional dynamics for different crystal lattices and crystallographic directions. Dynamics of the amplitude's propagation for different lattices and PFC mode's approximations is qualitatively compared. The traveling-wave velocity is quantitatively compared with data of molecular dynamics simulation previously obtained by Mendelev et al. [ Modell. Simul. Mater. Sci. Eng. 18, 074002 (2010)] for solidification and melting of the aluminum fcc lattice.