The development of edible films and coatings in the food packaging industry presents one of the modern strategies for protecting food products and ensuring their freshness and quality during their shelf lives. The application of microbial polysaccharides to the development of food package materials, as an alternative option to the commonly used plastic materials, is both economic and environmentally favorable. New edible films were developed using dextran from lactic acid bacterium Leuconostoc mesenteroides T3, and additionally plasticized by different concentrations of polyglycerol. The best tensile strength of the films was obtained using a formulation that contained 10 wt% of polyglycerol, which corresponded to a value of 4.6 MPa. The most flexible formulation, with elongation at break of 602%, was obtained with 30 wt% of polyglycerol. Water vapor permeability values of the films synthesized in this study were in the range of (3.45–8.81) ∗ 10⁻¹² g/m s Pa. Such low values indicated that they could be efficient in preventing fruit from drying out during storage. Thus, the film formulations were used to coat blueberries in order to assess their quality during a storage time of 21 days at 8 °C. The results showed that dextran/polyglycerol films could be efficient in extending the shelf life of blueberries, which was evidenced by lower weight loss and total sugar solids values, as well as a delay in titratable acidity, in comparison to the uncoated blueberries.

In the present study, supercritical solvent impregnation (SSI) has been applied to incorporate thymol into bio-composite polymers as a potential active packaging material. Thymol, a natural component with a proven antimicrobial activity, was successfully impregnated into starch-chitosan (SC) and starch-chitosan-zeolite (SCZ) films using supercritical carbon dioxide (scCO₂) as a solvent. Experiments were performed at 35 °C, pressures of 15.5 and 30 MPa, and an impregnation time in the range of 4–24 h. The highest impregnation yields of SC films with starch to chitosan mass ratios of 1:1 and 1:2 were 10.80% and 6.48%, respectively. The addition of natural zeolite (15–60%) significantly increased the loading capacity of films enabling thymol incorporation in a quantity of 16.7–27.3%. FTIR and SEM analyses were applied for the characterization of the films. Mechanical properties and water vapor permeability of films before and after the impregnation were tested as well. Thymol release kinetics in deionized water was followed and modeled by the Korsmeyer-Peppas and Weibull model. SCZ films with thymol loading of approximately 24% exhibited strong antibacterial activity against E. coli and methicillin-resistant Staphylococcus (S.) aureus (MRSA).