The reactivity of zinc in sodium hydroxide electrolytes containing sodium silicate and sodium tetraborate was studied by electrochemical and microstructural examinations. Impedance measurements indicate that a porous surface layer is formed on zinc immersed in sodium hydroxide at its open circuit potential and on polarization in the prepassive region. This surface layer becomes compact at potentials in the passive region. The anodic reactions of a zinc electrode in a sodium hydroxide containing electrolyte are controlled by the mass transport of zincate ions away from the electrode. Silicate and tetraborate ions suppress the anodic dissolution of zinc. In the presence of silicate ions, a compact silicate containing film is formed upon anodic polarization. The electrode rotation affects the microstructure of the surface layer both in silicate-free and silicate-containing sodium hydroxide solutions. On addition of tetraborate ions, the polarization resistance increases and the formation of a surface layer is achieved at increased applied potential.

The disposal of high-level radioactive waste (HLW) and spent nuclear fuel (SF) presents a unique challenge for the prediction of the long-term performance of corrodible structures since HLW/SF containers are expected, in some cases, to have lifetimes of one million years or longer. Various empirical and deterministic models have been developed over the past 45 years for making predictions of long-term corrosion behaviour, including models for uniform and localised corrosion, environmentally assisted cracking, microbiologically influenced corrosion, and radiation-induced corrosion. More recently, fracture-mechanics-based approaches have been developed to account for joint mechanical–corrosion degradation modes. Regardless of whether empirical or deterministic models are used, it is essential to be able to demonstrate a thorough mechanistic understanding of the corrosion processes involved. In addition to process models focused on specific corrosion mechanisms, there is also a need for performance-assessment models as part of the overall demonstration of the safety of a deep geological repository. Performance-assessment models are discussed in Part 2 of this review.

The disposal of high-level radioactive waste (HLW) and spent nuclear fuel (SF) presents a unique challenge for the prediction of the long-term performance of corrodible structures since the HLW/SF canisters are expected, in some cases, to have lifetimes of one million years or longer. Various empirical and deterministic models have been developed over the past 45 years for making predictions of the long-term corrosion behaviour, including models for uniform and localized corrosion, environmentally assisted cracking and microbiologically influenced corrosion. As well as process models focused on specific corrosion mechanisms (described in Part 1 of this review), there is also a need for performance assessment models as part of the overall analysis of the safety of a deep geological repository (DGR). Performance assessment models are often based on simplified or abstracted process models. The manner in which various international waste management programs have predicted the long-term performance of HLW/SF containers with copper, steel, Ni and Ti alloy corrosion barriers is discussed. Performance assessments are repeated periodically during the development and implementation of a DGR, and the corrosion models are constantly updated in light of new mechanistic understanding and/or more information about the deep geological environment. Two examples of how the container performance assessment models evolve over time are also described. Performance assessment models cannot easily be validated, so it is important to build confidence in the long-term predictions using other methods, including natural analogues and large-scale in situ tests and the use of complementary models.