Zinc ferrite nanocrystalline powder was obtained by solid state synthesis of starting zinc oxide and hematite nanopowders. Field emission scanning electron microscopy and transmission electron microscopy, X‐ray diffraction, X‐ray photoelectron spectroscopy and Raman spectroscopy confirmed the formation of nanocrystalline zinc‐ferrite powder with a mixed spinel structure with small amounts of remaining zinc oxide and hematite as impurities. Thick film paste was formed and screen printed on test interdigitated PdAg electrodes on alumina substrate. Formation of a porous nanocrystalline structure was confirmed by scanning electron microscopy and Hg porosimetry. Humidity sensing properties of zinc ferrite thick films were investigated by monitoring the change in impedance in the relative humidity interval 30%‐90% in the frequency range 42 Hz‐1 MHz at room temperature (25°C) and 50°C. At 42 Hz at both analyzed temperatures the impedance reduced ~46 times in the humidity range 30%‐90%. The dominant influence of grain boundaries was confirmed by analysis of complex impedance with an equivalent circuit.

Nanocomposites of polyvinylidene fluoride/polymethyl methacrylate (PVDF/PMMA) blend and mechanically activated barium titanate (BaTiO₃) particles were prepared by melt mixing. Modification of filler by means of mechanical activation has a profound effect on the crystallization of PVDF in the blend matrix. Raman analysis showed that the modified BaTiO₃ particles, due to higher specific surfaces, induce, predominantly, the crystallization of the electrically active β-phase of PVDF, while the initial micron size particles induce the formation of the most common but non-polar α-crystal form. The introduction of activated particles reduces the overall crystallinity but slightly affects the crystallization and melting temperatures of the matrix. Dielectric spectroscopy revealed that at fixed filler content the dielectric constant of the blend increases with decreasing of the particle size (increasing of the activation time). A similar trend was observed for the storage moduli in dynamic mechanical analysis; the stiffness of the composite was higher when mechanically activated particles were used.