Researchers have been driven to investigate sustainable alternatives to cement production, such as geopolymers, due to the impact of global warming and climate change resulting from greenhouse gas emissions. Currently, they are exploring different methods and waste materials to enhance the mechanical and physical properties of geopolymer and expand its application range. This review paper offers a thorough analysis of the utilization of various waste materials in geopolymer manufacturing and shows the creative contribution of this research to the development of environmentally friendly cement substitutes. The article covers the properties, durability, and practical applications of geopolymer composites made from various waste binders. It includes a microstructure and chemical analysis. The research findings indicate that geopolymers are an effective cementitious binder substitute for cement in various applications. Additionally, the ecological and carbon footprint analysis highlights the sustainability of geopolymers compared to cement.

This paper presents an investigation on lightweight foamed concrete (LFC) with different type of additives. LFC with 600, 1000 and 1400 kg/m³ density were cast and tested. Fly ash, lime and polypropylene fibre were used on each density with different percentages. All the additives effects were compared with normal LFC as control mix. Mechanical properties of LFC were evaluated with several tests up to 180 days. The results show that the drying shrinkage, compressive strength and flexural strength are affected by the hydration process of each additive in the harden LFC. Fly ash as pozzolanic material helps to strengthen the LFC, though it needs longer curing period to achieve ultimate strength. Lime gives slight contribution to strength as detail investigation on microstructure formation will give clear answer on how the mechanical properties were affected. The addition of polypropylene contributes to flexural strength and shrinkage of LFC. Polypropylene fibre only contributes to compressive strength at low LFC density.