A simple method of synthesis of high pure tris(8-hydroxyquinoline)aluminum (Alq₃) from commercial available 5N Al₂O₃ and 8-hydroxyquinolinol has been developed. One-step exchange chemical reaction has been conducted under controlled 8-hydrixyquinoline vapor at a temperature of 190–240 °C with water removal by phosphorus anhydride. According to analysis of inductively coupled plasma mass-spectrometry, the chemical purity of synthesized Alq₃ was 99.998 wt%. Photoluminescence of the synthesized Alq₃ has been measured and slightly differed from those of Alq₃ obtained by traditional organic synthesis.

The strong influence of MoO ₃ chemical purity from 99.99 wt% to 99.999 wt% on lithium triborate (LBO) and NaLa(MoO ₄ ) ₂ crystal growth as well as on OLED technologies has been demonstrated.

A new luminescent hybrid material based on silica aerogel and a boron-containing coordination compound with 8-hydroxyquinoline was created, and its physicochemical and spectral-luminescent characteristics were studied. A simple scheme for the synthesis of a hybrid luminescent material was developed. Simultaneously with the synthesis of the aerogel, the formation of a boron-containing phosphor was carried out using an isopropanol solution of boric acid and 8-hydroxyquinoline. Using in situ luminescent measurements, the mechanisms of the formation of boron-based luminescent complexes in isopropanol and tetrahydrofuran media were established. Both hydrophilic and hydrophobic silica aerogels were tested as matrices for the hybrid material. The formation of a thin layer of a boron-containing coordination luminescent compound on the highly developed surface of the SiO₂ aerogel made it possible to strongly stabilize the aerogel structure and noticeably increase the thermal stability of the synthesized hybrid material.