Zein, a subproduct of the food industry and a protein, possesses limited applications due to its high hydrophobic character. The objective of this research was to investigate the influence of homogenization pressure and cycles on the volumetric mean diameter (D_4,3), span values, and Turbiscan Stability Index (TSI) using the response surface methodology for microfluidized emulsions containing zein as a unique stabilizer. Results showed that homogenization pressure seems to be the most influential parameter to obtain enhanced physical stability and droplet size distributions, with the optimum being 20,000 psi. Interestingly, the optimum number of cycles for volumetric diameter, span value, and TSI is not the same. Although a decrease of D_4,3 with number of cycles is observed (optimum three cycles), this provokes an increase of span values (optimum one cycle) due to the recoalescence effect. Since physical stability is influenced by D_4,3 and span, the minimum for TSI is observed at the middle level of the cycles (2 cycles). This work highlights that not only volumetric diameter, but also span value must be taken into consideration in order to obtain stable zein emulsions. In addition, this study wants to extend the limited knowledge about zein-based emulsions processed with a Microfluidizer device.

Titanium is widely used for implants however it presents limitations such as infection risk, stress shielding phenomenon, and poor osseointegration. To address these issues, a novel approach was proposed that involves fabricating porous titanium substrates, to reduce implant stiffness, minimizing stress shielding and bone resorption, and applying polymeric coatings to improve bioactivity. Composite coating prepared from chitosan, silver nanoparticles, and nanohydroxyapatite was optimized to enhance antibacterial properties and promote osseointegration. Chitosan with 80.5 % of deacetylation degree was used to prepare composites with diverse compositions, including different methodologies of adding silver nanoparticles, with silver concentrations below toxic level. Antibacterial activity was tested with three different strains, including Gram+ and Gram- bacteria, demonstrating excellent inhibition after 21 days. In addition, the induction of hydroxyapatite formation was investigated. Finally, the optimal porous metallic substrate that exhibited a more suitable stiffness (29 GPa) (close to the cortical bone tissue they intend to replace) was chosen to be infiltrated with the selected composites. In summary, this synergistic approach based on the combination of porous titanium substrates with 60 vol% porosity and a 355-500 μm pore size distribution coated with 3%CS-nHA-AgNPs-TPP-AgNPs_bath composite provided a potential solution to provide implants with improved biomechanical balance and biofunctionality.