The Lewis/Brønsted catalytic properties of the Metal–Organic Framework (MOF) nodes can be tuned by simply controlling the solvent employed in the synthetic procedure. In this work, we demonstrate that Hf-MOF-808 can be prepared from a material with a higher amount of Brønsted acid sites, via modulated hydrothermal synthesis, to a material with a higher proportion of unsaturated Hf Lewis acid sites, via modulated solvothermal synthesis. The Lewis/Brønsted acid properties of the resultant metallic clusters have been studied by different characterization techniques, including XAS, FTIR and NMR spectroscopies, combined with a DFT study. The different nature of the Hf-MOF-808 materials allows their application as selective catalysts in different target reactions requiring Lewis, Brønsted or Lewis–Brønsted acid pairs.

The development of active and selective non-noble metal-based catalysts for the chemoselective reduction of nitro compounds in aquo media under mild conditions is an attractive research area. Herein, the synthesis of subnanometric and stable cobalt nanoclusters, covered by N-doped carbon layers as core–shell (Co@NC-800), for the chemoselective reduction of nitroarenes is reported. The Co@NC-800 catalyst was prepared by the pyrolysis of the Co(tpy)₂ complex impregnated on Vulcan carbon. In fact, the use of a molecular complex based on six N–Co bonds drives the formation of a well-defined and distributed cobalt core–shell nanocluster covered by N-doped carbon layers. In order to elucidate its nature, it has been fully characterized by using several advanced techniques. In addition, this as-prepared catalyst showed high activity, chemoselectivity and stability toward the reduction of nitro compounds with H₂ and under mild reaction conditions; water was used as a green solvent, improving the previous results based on cobalt catalysts. Moreover, the Co@NC-800 catalyst is also active and selective for the one-pot synthesis of secondary aryl amines and isoindolinones through the reductive amination of nitroarenes. Finally, based on diffraction and spectroscopic studies, metallic cobalt nanoclusters with surface CoN_x patches have been proposed as the active phase in the Co@NC-800 material.