Spatially resolved, time-integrated optical emission spectroscopy was applied for investigation of copper plasma produced by a nanosecond infrared (IR) transversely excited atmospheric (TEA) CO₂ laser, operating at 10.6 μm. The effect of surrounding air pressure, in the pressure range 0.1 to 1013 mbar, on plasma formation and its characteristics was investigated. A linear dependence of intensity threshold for plasma formation on logarithm of air pressure was found. Lowering of the air pressure reduces the extent of gas breakdown, enabling better laser-target coupling and thus increases ablation. Optimum air pressure for target plasma formation was 0.1 mbar. Under that pressure, the induced plasma consisted of two clearly distinguished and spatially separated regions. The maximum intensity of emission, with sharp and well-resolved spectral lines and negligibly low background emission, was obtained from a plasma zone 8 mm from the target surface. The estimated excitation temperature in this zone was around 7000 K. The favorable signal to background ratio obtained in this plasma region indicates possible analytical application of TEA CO₂ laser produced copper plasma. Detection limits of trace elements present in the Cu sample were on the order of 10 ppm (parts per million). Time-resolved measurements of spatially selected plasma zones were used to find a correlation between the observed spatial position and time delay. Index Headings: Laser induced Cu-plasma emission; Shock wave plasma; Copper target; Transversely excited atmospheric CO₂ laser; TEA CO₂ laser.

Today, hydrogel dressings that can protect injury sites and effectively promote healing have become highly desirable in wound management. Therefore, multifunctional silver-poli(N-isopropylacrylamide/itaconic acid) (Ag-P(NiPAAm/IA)) hydrogel nanocomposites were developed for potential application as topical treatment dressings. The radiolytic method, used for the crosslinking of the polymer matrix as well as for the in situ incorporation of silver nanoparticles (AgNPs) into the polymer matrix, enables the preparation of hydrogel nanocomposites without introducing harmful and toxic agents. Moreover, materials produced using γ-irradiation are simultaneously sterilized, thus fulfilling one of the basic requirements regarding their potential biomedical applications. The NiPAAm/IA ratio and the presence of AgNPs influenced the microstructural parameters of the investigated systems. Increasing the IA content leads to the formation of a more porous polymer matrix with larger pores, while the incorporated AgNPs act as additional junction points, decreasing the porosity and pore size of the resulting nanocomposite hydrogels. Swelling studies showed that most investigated systems uptake the fluids from their surroundings by non-Fick diffusion. Further, the Ag⁺ ion release, antibacterial activity, and cytotoxicity of Ag-P(NiPAAm/IA) hydrogel nanocomposites were examined to evaluate their biomedical potential. All hydrogel nanocomposites showed an initial burst release of Ag⁺ ions (useful in preventing bacteria adherence and biofilm formation), followed by a slower release of the same (ensuring sterility for longer use). An antibacterial activity test against Escherichia coli and Staphylococcus aureus showed that Ag-P(NiPAAm/IA) hydrogel nanocomposites, with silver concentrations around 10 ± 1 ppm, successfully prevent bacterial growth. Finally, it was shown that the investigated hydrogel nanocomposites do not exhibit a cytotoxic effect on human keratinocyte HaCaT cells. Therefore, these multifunctional hydrogel nanocomposites may promote wound repair and show promising potential for application as functional wound dressing.

The effect of potassium addition on the radial distribution of temperature and electron number density in a U-shaped direct current (dc) argon plasma operating at different arc currents has been studied by optical emission spectroscopic techniques and the power interruption method. Spatially resolved electron number densities (n _e) have been determined from measured radial profiles of Balmer-H_β spectral line. The obtained electron number densities have been used for thermodynamic temperature (T _LTE) evaluation with the assumption that the arc plasma is in a state of local thermodynamic equilibrium. The excitation temperatures (T _exc) have been determined from the absolute integral emissivity of the argon line at 430.01 nm. For heavy particle temperature (T _h) evaluations we have used a power interruption method. The obtained results have shown that an addition of KCl decreases both electron number density and temperature of the arc column. The magnitude of such an influence on plasma parameters increases with an increase in the KCl concentration and decreases with an increase in the arc current.