Oligo(L-lactic acid) (OLLA) was synthesized by ring opening polymerization of L-lactides using stannous octoate (0.03 wt% of lactide). While this served as the initiator, L-lactic acids were the co-initiators at 140 °C for 10 h, wherein L-lactic acids were prepared by hydrolytic degradation of L-lactides at 100 °C for 1 h. The molecular weight or degree of polymerization was controlled with monomer/co-initiator ratio (mol/mol). α-cellulose and microcrystalline cellulose (MCC) were extracted from jute fiber by subsequent treatment with sodium chlorite (Na₂ClO₂), NaOH and H₂SO₄. Grafting of OLLA onto α-cellulose and MCC in toluene was carried out using para-toluene sulphonic acid as a catalyst and potassium persulphate (KPS) as an initiator at 130 °C under 380 mm (Hg) pressure for 3, 6, 9, 12, 15, and 18 h. New properties of α-cellulose and MCC were observed due to the successful grafting onto α-cellulose and MCC. Fourier-transform infrared spectroscopy (FTIR) and scanning electron microscope (SEM) were conducted in order to confirm grafting of OLLA onto cellulose and MCC. The FTIR analysis results showed there are some new characteristic absorption peaks appeared (1728 to 1732 cm⁻¹) in the spectrum, which confirmed the grafting of OLLA onto α-cellulose and MCC was successful. SEM images of α-cellulose and MCC before and after grafting revealed significant changes in surface morphology. Grafting of MCC could be more effective for further application in comparison to α-cellulose.