This statistical review compares the crystallographic structures of functional nanocrystals composed of silver (Ag), copper (Cu) and titanium (Ti) using transmission electron microscopy (TEM) and X-ray diffraction (XRD) analyses. TEM provides high-resolution imaging to directly visualize individual nanoparticles' size, internal shape and crystallinity. Statistical analysis quantifies variations in lattice parameters, crystal structure, size distributions, phase compositions, lattice strains, preferred orientation and lattice volume of these three crystalline nanomaterials. The review highlights the complementary roles of TEM and XRD in comprehensive Ag, Cu and Ti nanocrystalline materials characterization. The crystallographic functional parameters of Ag were 2θ= 38.1° (111), 44.3° (200) and 64.4° (220); for Cu crystal 43.3° (111), 50.4° (200), 74.1° (220), 89.9° (311) and 95.1° (222) and 35.1° (100), 38.4° (002), 40.2° (101), 53.0° (102), 63.0° (103), 70.7° (110), 76.2° (112), 82.3° (201) demonstrated for Ti nanocrystals. The crystallographic predominant plane or Miller indices were also revealed by selected area electron diffraction (SAED) on TEM. The FCC structure of Ag and Cu is shown in larger lattice volumes compared to the HCP structure of Ti and prefer oriented. The degree of crystallinity of Ti, Cu and Ag nanocrystalline materials was observed at 90.0%, 98.0% and 100.0% respectively. This quantitative comparison provides valuable insights into the structural property relationships in these nanocrystals, enabling rational design strategies for optimizing their performance in various functional applications.

Oligo(L-lactic acid) (OLLA) was synthesized by ring opening polymerization of L-lactides using stannous octoate (0.03 wt% of lactide). While this served as the initiator, L-lactic acids were the co-initiators at 140 °C for 10 h, wherein L-lactic acids were prepared by hydrolytic degradation of L-lactides at 100 °C for 1 h. The molecular weight or degree of polymerization was controlled with monomer/co-initiator ratio (mol/mol). α-cellulose and microcrystalline cellulose (MCC) were extracted from jute fiber by subsequent treatment with sodium chlorite (Na₂ClO₂), NaOH and H₂SO₄. Grafting of OLLA onto α-cellulose and MCC in toluene was carried out using para-toluene sulphonic acid as a catalyst and potassium persulphate (KPS) as an initiator at 130 °C under 380 mm (Hg) pressure for 3, 6, 9, 12, 15, and 18 h. New properties of α-cellulose and MCC were observed due to the successful grafting onto α-cellulose and MCC. Fourier-transform infrared spectroscopy (FTIR) and scanning electron microscope (SEM) were conducted in order to confirm grafting of OLLA onto cellulose and MCC. The FTIR analysis results showed there are some new characteristic absorption peaks appeared (1728 to 1732 cm⁻¹) in the spectrum, which confirmed the grafting of OLLA onto α-cellulose and MCC was successful. SEM images of α-cellulose and MCC before and after grafting revealed significant changes in surface morphology. Grafting of MCC could be more effective for further application in comparison to α-cellulose.