This paper is focused on the utilisation of double edge notched tension, staggered and shear tests to determine fracture toughness and the formability limits by fracture in principal strain space. The experiments were performed in test specimens with different geometries and ligament angles, and the influence of strain hardening was taken into consideration by selecting two materials (aluminium AA1050-H111 and pure copper), with very different strain hardening exponents. Results are plotted in principal strain space, and the discussion is focused on the link between formability limits, fracture toughness and macroscopic fractography characteristics of the specimens that fail by mode I, mode II or mixed-mode.

Lattice structures are a prime candidate for applications in the medical implant industry due to their versatile mechanical behaviour, which can be tailored to meet specific patient needs and reduce stress shielding, while enabling the natural flow of body fluids. In this work, the mechanical properties of metallic lattices made of five different unit cell types, Cubic (C), Truncated Octahedron (TO), Truncated Cubic (TC), Rhombicuboctahedron (RCO), and Rhombitruncated Cuboctahedron (RTCO), were evaluated under uniaxial compression at three different relative densities, 5%, 15%, and 45%. The evaluation was experimental, and it was compared with previous and new finite element simulations. Specimens for the experimental tests were fabricated in stainless steel 316L by laser powder bed fusion, and stress–strain curves were obtained for the different lattices. The combination of the test results with a critical interpretation of the deformation mechanisms allowed us to confirm that two unit cell types, TO and RTCO, are stable for the whole range of relative densities evaluated. The other three unit cells exhibit more unpredictable behaviour, either due to manufacturing defects or limitations, or because their unstable compression behaviour leads to bucking. For these reasons, TO and RTCO unit cell types are mechanically more adequate for applications in the medical implant industry.

Laser powder bed fusion (L-PBF) is one of the most promising additive manufacturing technologies for creating customised 316L Stainless Steel (SS) implants with biomimetic characteristics, controlled porosity, and optimal structural and functional properties. However, the behaviour of as-fabricated 3D 316L SS structures without any surface finishing in environments that simulate body fluids remains largely unknown. To address this knowledge gap, the present study investigates the surface characteristics, the internal porosity, the corrosion in simulated body fluid (SBF), and the mechanical properties of as-fabricated 316L SS structures manufactured by L-PBF with rhombitruncated cuboctahedron (RTCO) unit cells with two distinct relative densities (10 and 35%). The microstructural analysis confirmed that the RTCO structure has a pure austenitic phase with a roughness of ~20 µm and a fine cellular morphology. The micro-CT revealed the presence of keyholes and a lack of fusion pores in both RTCO structures. Despite the difference in the internal porosity, the mechanical properties of both structures remain within the range of bone tissue and in line with the Gibson and Ashby model. Additionally, the as-fabricated RTCO structures demonstrated passive corrosion behaviour in the SBF solution. Thus, as-fabricated porous structures are promising biomaterials for implants due to their suitable surface roughness, mechanical properties, and corrosion resistance, facilitating bone tissue growth.

Additive manufacturing, particularly using Laser Powder Bed Fusion (LPBF) technologies with 316L stainless steel, has proven highly promising in biomedical engineering due to the material’s exceptional mechanical properties and biocompatibility. This study, which is a foundational step towards developing porous bone implants, focuses on assessing the influence of a broad range of parameters - spot size, scanning speed, laser power, and energy density - on the mechanical performance and structural integrity of 316L stainless steel parts across three distinct specimen geometries: fully dense parallelepipedic, fully dense cubic, and cellular (lattice) specimens. By analysing 17 different parameter sets and producing over 150 specimens, a thorough series of experimental tests were conducted, including flexural tests, compression tests, hardness tests, macroscopic evaluation of the surface of fully dense specimens, and macroscopic evaluation of the lattice structures.e in powder accumulation within the pores of cellular structures, with higher energy densities (100 J/mm ³ ) leading to a significantly greater retention compared to lower energy densities (66 J/mm ³ ). This underexplored phenomenon has significant implications for the selection of parameters in the fabrication of bone implants. Further research is needed to refine LPBF printing parameters and enhance the quality of porous bone implants.