Magnetic graphene oxide was impregnated with polymers for the preparation of nanocomposite adsorbents to be examined for the adsorptive removal of a typical endocrine disruptor, bisphenol–A (BPA) from aqueous solutions. The polymers used were polystyrene, chitosan and polyaniline. The nanocomposites prepared were characterized for their structure, morphology and surface chemistry. The nanocomposites presented an increase adsorptive activity for BPA at ambient conditions, compared to pure magnetic oxide, attributed to the synergistic effect of the polymers and the magnetic graphene oxide. The increased adsorption of BPA exhibited by the nanocomposites with chitosan and polyaniline could be attributed to the contribution of amine groups.

Sodium hydroxide-modified graphene oxide was used as manganese oxides support for the preparation of nanocomposites via a one-pot preparation route for the degradation of Reactive Black 5. The nanocomposites were characterized for their structure by X-ray diffraction, for their textural properties by Nitrogen adsorption, and for their surface chemistry by Fourier transform infrared spectroscopy, potentiometric titration, and thermal analysis measurements. The nanocomposites prepared showed to possess high activity for the degradation/oxidation of Reactive Black 5 at ambient conditions, without light irradiation, which was higher than that of the precursors manganese oxides and can be attributed to the synergistic effect of the manganese oxides and the modified graphene oxide.

The aim of the present study is the synthesis of activated carbon (AC) from different agricultural wastes such as tea and plane tree leaves in order to use them for the removal of pramipexole dihydrochloride (PRM) from aqueous solutions. Two different carbonization and synthetic activation protocols were followed, with the herein-proposed ultrasound-assisted two-step protocol leading to better-performing carbon, especially for the tea-leaf-derived material (TEA(char)-AC). Physicochemical characterizations were performed by Fourier-transform infrared spectroscopy (FTIR), N₂ physisorption, and scanning electron microscopy (SEM). TEA(char)-AC presented the highest surface area (1151 m²/g) and volume of micro and small mesopores. Maximum capacity was found at 112 mg/g for TEA(char)-AC at an optimum pH equal to 3, with the Langmuir isotherm model presenting a better fitting. The removal efficiency of TEA(char)-AC is higher than other biomass-derived carbons and closer to benchmark commercial carbons.

The aim of the present study was to synthesize various samples of activated carbon (AC) from different agricultural sources as precursors, like orange peels, tea stalks, and kiwi peels, as well as sucrose. The synthesis of AC was achieved with chemical activation using H₃PO₄ and KOH. The produced AC samples were tested as adsorbents for the removal of a pharmaceutical model compound, pramipexole dihydrochloride (PRM), from synthetic aqueous synthetic solutions. The produced-from-sucrose AC presented the higher yield of synthesis (~58%). The physicochemical features of the materials were analyzed by FTIR spectroscopy, N₂ physisorption, and SEM imaging. More specifically, the AC sample derived from sucrose (SG-AC) had the highest specific surface area (1977 m²/g) with the total pores volume, mesopores volume, and external surface area being 1.382 cm³/g, 0.819 cm³/g, and 751 m²/g, respectively. The effect of the initial pH and PRM concentration were studied, while the equilibrium results (isotherms) were fitted to Langmuir and Freundlich models. The maximum adsorption capacities were found to be 213, 190, 155, and 115 mg/g for AC samples produced from sucrose, kiwi peels, orange peels, and tea stalks, respectively.