The efficiency of membrane reactors for steam reforming of hydrocarbons depends critically on the performance and selectivity of hydrogen-permeable membranes. In this work, a strategy for controlling the catalytic and gas-transport characteristics of Pd-Ag-Ru membranes by modifying the surface and controlling the morphology of nanostructured coatings was developed. It was found that as the process temperatures approached ~200 °C and the membrane thickness decreased, a transition to limitation of the hydrogen transfer process by surface stages was observed. Surface modification with pyramidal nanoparticles resulted in a significant increase in the hydrogen flux by up to 1.5 times compared to membranes with spiked nanoparticles and up to 2 times compared to membranes with spherical nanoparticles. The maximum difference in fluxes of up to 12 times was achieved compared to uncoated membranes. The achieved result is due to a significant increase in the active surface area associated with a systematic change in the morphology of the coatings. This aspect was a key factor in improving the catalytic activity of the material, reducing the energy barrier of sorption and accelerating the stages of hydrogen transfer through the developed membranes. Thus, modification with shape-controlled nanoparticle coatings presents an effective strategy for overcoming the limitations of the permeability of palladium-based membranes under conditions of small thickness and low temperatures. The use of the developed membranes in steam reforming reactors of alcohols can provide increased energy efficiency, conversion and purity of hydrogen.

The non-trivial topology of electronic bands in Weyl semimetals originates from band inversion due to strong spin–orbit coupling. The Weyl semimetals have pairs of Weyl gap-less nodes in the bulk Brillouin zone. The tungsten ditelluride WTe₂ likely belongs to type II Weyl semimetals. Doping WTe₂ with magnetic ions could induce magnetic ordering in this crystal, which provides prospects for practical applications. We studied the magnetic properties of the iron-doped single crystals Fe_0.03W_0.97Te₂, annealed and unannealed, in comparison with the undoped WTe₂. Measurements of the dc magnetization were carried out from 1.8 to 400 K. We revealed pronounced ferromagnetic ordering that was affected by annealing. Anomalies associated with antiferromagnetism and paramagnetism were also found. The magnetic order was suppressed by a field of 60 kOe. The rise in susceptibility with increasing temperature was observed at high temperatures in all samples and was treated using a model developed for Weyl semimetals. The Curie–Weiss law fit at 60 kOe showed that the effective magnetic moment was close to that of Fe²⁺. Metamagnetism was demonstrated for the unannealed doped WTe₂ crystal. The data for the heat capacity of the iron-doped sample agreed with results for the undoped WTe₂.