In this study, we present an alternative method for synthesizing carbon quantum dots (CQDs) using a green synthesis approach via extracts from Agave maximiliana and Opuntia ficus-indica (Ofi). The extracts from both plants were used as the carbon source for the CQDs. The synthesis method employs mesoporous zeolite 4A as a refractory for the thermal treatment of the samples. Transmission electron microscopy analysis established that the size of the CQDs shows a narrow distribution centered around 2 nm with a maximum size of less than 3 nm for both cases. The CQDs exhibit absorption bands associated with p-p* transitions located around 220 nm. In both cases, photoluminescence (PL) phenomenon was detected by irradiating the samples with a UV wavelength and detecting emissions close to the blue wavelength. Additionally, both kinds of CQDs were tested as surface-enhanced Raman scattering (SERS) substrates against methylene blue (MB), indicating an enhancement associated with ring deformation and stretching modes of the v(C-C) and v(C-N) bonds located around 1400 and 1620 cm(-1), respectively. Complementarily, in the framework of density functional theory, H-2n C2(2m+1) structures (with n = 3-5 and m = 1-3) were used as a theoretical representation of CQDs in interaction with the MB molecule. It is used for developing the analysis of charge transfer effects between both systems and for specifying elements that generate the SERS effect associated with the chemical enhancement mechanism.

Hybrid coatings of SiO₂ and recycled unsaturated polyester resin (R-UPR) from recycled polyethylene-terephthalate (PET) were prepared by the sol-gel process on glass substrates. First, SiO₂ was synthesized by the sol-gel process using a tetraethyl orthosilicate (TEOS) solution. Next, bis(2-hydroxypropyl-terephthalate) (BHPT) was synthesized from mechanical and chemical recycling (glycolysis) of post-consumer PET bottles in propylene glycol (PG) using ZnA as catalyst, in a Vessel-type reactor (20–200 °C); maleic anhydride (MA) was added and, following the same procedure, the unsaturated polyester (UP) was synthetized, which was cooled to room temperature. Next, styrene (St) and benzoyl-peroxide (PBO)-initiator were added to obtain R–UPR. TEOS (T) and three hybrid solutions were synthesized, with molar ratios of 0:1:0 (T), 1:2:0.25 (H1), 1:1:0.25 (H2), and 1:0:0.25 (H3) for R–UPR:TEOS:3-trimethoxy-(silyl)-propyl-methacrylate (TMSPM), respectively, with which TC, HC1, HC2, and HC3 coatings were elaborated using the immersion technique and polymerized (120 °C for 24 h). The solutions were characterized by FT–IR and TGA, and the coatings by SEM, nanoindentation, AFM, adhesion, and contact angle. The results showed that SiO₂ enhanced mechanical (hardness and Young’s modulus) and thermal properties of the R-UPR. The coatings adhered perfectly to the substrate, with thicknesses of micrometer units and a flat surface; in addition, hydrophilicity decreased as SiO₂ decreased.