Hybrid coatings of SiO₂ and recycled unsaturated polyester resin (R-UPR) from recycled polyethylene-terephthalate (PET) were prepared by the sol-gel process on glass substrates. First, SiO₂ was synthesized by the sol-gel process using a tetraethyl orthosilicate (TEOS) solution. Next, bis(2-hydroxypropyl-terephthalate) (BHPT) was synthesized from mechanical and chemical recycling (glycolysis) of post-consumer PET bottles in propylene glycol (PG) using ZnA as catalyst, in a Vessel-type reactor (20–200 °C); maleic anhydride (MA) was added and, following the same procedure, the unsaturated polyester (UP) was synthetized, which was cooled to room temperature. Next, styrene (St) and benzoyl-peroxide (PBO)-initiator were added to obtain R–UPR. TEOS (T) and three hybrid solutions were synthesized, with molar ratios of 0:1:0 (T), 1:2:0.25 (H1), 1:1:0.25 (H2), and 1:0:0.25 (H3) for R–UPR:TEOS:3-trimethoxy-(silyl)-propyl-methacrylate (TMSPM), respectively, with which TC, HC1, HC2, and HC3 coatings were elaborated using the immersion technique and polymerized (120 °C for 24 h). The solutions were characterized by FT–IR and TGA, and the coatings by SEM, nanoindentation, AFM, adhesion, and contact angle. The results showed that SiO₂ enhanced mechanical (hardness and Young’s modulus) and thermal properties of the R-UPR. The coatings adhered perfectly to the substrate, with thicknesses of micrometer units and a flat surface; in addition, hydrophilicity decreased as SiO₂ decreased.

A new, sustainable polypropylene terephthalate (PPT) coating was synthesized from recycled polyethylene terephthalate (PET) and applied onto a hydraulic concrete substrate to improve its durability. For the first step, PET bottle wastes were ground and depolymerized by glycolysis using propylene glycol (PG) in a vessel-type reactor (20–180 °C) to synthesize bis(2-hydroxypropyl)-terephthalate (BHPT), which was applied as a coating to one to three layers of hydraulic concrete substrate using the brushing technique and polymerized (150 °C for 15 h) to obtain PPT. PET, BHPT, and PPT were characterized by FT-IR, PET, and PPT using TGA, and the PPT coatings by SEM (thickness), ASTM-D3359-17 (adhesion), and water contact angle (wettability). The durability of hydraulic concrete coated with PPT was studied using resist chloride ion penetration (ASTM-C1202-17), carbonation depth at 28 days (RILEM-CPC-18), and the absorption water ratio (ASTM-C1585-20). The results demonstrated that the BHPT and PPT were synthetized (FT-IR), and PPT had a similar thermal behavior to PET (TGA); the PPT coatings had good adhesion to the substrate, with thicknesses of micrometric units. PPT coatings presented hydrophilic hydrophilic behavior like PET coatings, and the durability of hydraulic concrete coated with PPT (2–3 layers) improved (migration of chloride ions decreased, carbonation depth was negligible, and the absorption water ratio decreased).