Silver powders chemically synthesized by reduction with hydrazine and those produced by electrolysis from the basic (nitrate) and complex (ammonium) electrolytes were examined by X-ray diffraction (XRD) and scanning electron microscopic (SEM) analysis of the produced particles. Morphologies of the obtained particles were very different at the macro level. The needle-like dendrites, as well as the mixture of irregular and regular crystals, were formed from the nitrate electrolyte, while the highly-branched pine-like dendrites with clearly noticeable spherical grains were formed from the ammonium electrolyte. The agglomerates of spherical grains were formed by reduction with hydrazine. In the particles obtained from the nitrate electrolyte, Ag crystallites were strongly oriented in the (111) plane. Although morphologies of Ag particles were very different at the macro level, the similarity at the micro level was observed between chemically-synthesized particles and those obtained by electrolysis from the ammonium electrolyte. Both types of particles were constructed from the spherical grains. This similarity at the micro level was accompanied by the similar XRD patterns, which were very close to the Ag standard with a random orientation of Ag crystallites. For the first time, morphologies of powder particles were correlated with their crystal structure.

Hydroxyapatite attracts great attention as hard tissues implant material for bones and teeth. Its application in reconstructive medicine depends on its biocompatibility, which is in a function of composition and surface properties. The insertion of a protein element in the composition of implants can improve the cell adhesion and the osseointegration. Having this in mind, the proposal of this work was to develop L-alanine-grafted hydroxyapatite nanoparticles and to study their biocompatibility. Two L-alanine sources and three grafting methods were used for hydroxyapatite surface functionalization. The efficiency of grafting was determined based on X-ray powder diffraction, Fourier-transform infrared spectroscopy, thermal analyses, and field-emission scanning electron microscopy. The results indicated the formation of hydroxyapatite with 8–25 wt% of organic content, depending on the grafting method. Protein adsorption, cell adhesion, and viability studies were carried out to evaluate biological properties of grafted materials. The viability of MG-63 human osteoblastic cells following 24 h incubation with the alanine-grafted hydroxyapatite samples is well preserved, being in all cases above the viability of cells incubated with hydroxyapatite. The alanine-grafted hydroxyapatite prepared in situ and by simple mixture showed higher protein adsorption and cell adhesion, respectively, indicating their potential toward use in regenerative medicine.