The coemulsification method suitable for the formulation of microcapsules of n-eicosane coated with a polysiloxane is developed. This method allows to synthesize core–shell microcapsules of paraffin which have the shape of spheres or distorted spheres and are designed for the use as phase change materials. The microcapsules are formed in aqueous phase by the precipitation of n-eicosane together with modified polyhydromethylsiloxane from a common solvent which is miscible with aqueous media. The polysiloxane is modified by the attachment of silylvinyl and alkoxy functions before coemulsification with the paraffin. It also contains the Pt(0) Karstedt catalyst. The microcapsules formed by coemulsification are stabilized by the in situ cross-linking of the polysiloxane shell. The shell is additionally modified by the in situ generation of silanol groups which provide colloidal stabilization of microspheres in aqueous phase. Microcapsules were studied by DSC, SEM, optical polarized microscope, and by thermooptical analysis (TOA).

Cotton fabrics were modified by xerogel coatings with dispersed particles of graphene (Gr) or reduced graphene oxide (RGO). To obtain a stable dispersion of Gr or RGO in organo-silicon sol, sodium lauryl sulfate as an anionic surfactant was used. The fabrics were padded with the organo-silicon sol containing dispersed Gr or RGO, forming a thin xerogel coating after drying. The fabrics coated with the xerogel containing 0.5–1.5 wt% of RGO or Gr were prepared and examined. The best anti-static properties were obtained for the coating with 1.5 wt% of Gr, whose surface resistance and volume resistance were on the order of 10⁵ and 10³ Ω, respectively. Such properties make the fabric suitable for protective cloths in the environment with explosive atmosphere.