Graphitic carbon is a valuable material that can be utilized in many fields, such as electronics, energy storage and wastewater filtration. Due to the high demand for commercial graphite, an alternative raw material with lower costs that is environmentally friendly has been explored. Amongst these, an agricultural bio-waste material has become an option due to its highly bioactive properties, such as bioavailability, antioxidant, antimicrobial, in vitro and anti-inflammatory properties. In addition, biomass wastes usually have high organic carbon content, which has been discovered by many researchers as an alternative carbon material to produce graphite. However, there are several challenges associated with the graphite production process from biomass waste materials, such as impurities, the processing conditions and production costs. Agricultural bio-waste materials typically contain many volatiles and impurities, which can interfere with the synthesis process and reduce the quality of the graphitic carbon produced. Moreover, the processing conditions required for the synthesis of graphitic carbon from agricultural biomass waste materials are quite challenging to optimize. The temperature, pressure, catalyst used and other parameters must be carefully controlled to ensure that the desired product is obtained. Nevertheless, the use of agricultural biomass waste materials as a raw material for graphitic carbon synthesis can reduce the production costs. Improving the overall cost-effectiveness of this approach depends on many factors, including the availability and cost of the feedstock, the processing costs and the market demand for the final product. Therefore, in this review, the importance of biomass waste utilization is discussed. Various methods of synthesizing graphitic carbon are also reviewed. The discussion ranges from the conversion of biomass waste into carbon-rich feedstocks with different recent advances to the method of synthesis of graphitic carbon. The importance of utilizing agricultural biomass waste and the types of potential biomass waste carbon precursors and their pre-treatment methods are also reviewed. Finally, the gaps found in the previous research are proposed as a future research suggestion. Overall, the synthesis of graphite from agricultural bio-waste materials is a promising area of research, but more work is needed to address the challenges associated with this process and to demonstrate its viability at scale.

Two different phases of alumina (Al2O3) nanoparticles (γ-alumina and α-alumina) have successfully been synthesized by using a sol-gel method. During the process a mixture of aluminum nitrate and citric acid (C/N=0.5) was heated at 60°C followed by 80°C until a gel was formed. The amorphous gel structure then was dried and sintered from 600°C to 1200°C. From the X-ray diffraction (XRD) analysis, crystalline structure of γ-alumina started to form at 800°C with average crystallite size of 11.5 nm, followed by the formation of the mixture phase of γ-alumina and α-alumina at 1000°C. The transformation from γ- to α-alumina occured at 1100°C of sintering temperature and above with the average crystallite size of 49 nm. The efficiency of the synthesized alumina nanoparticles as an adsorbents was tested by immersing the powder into the copper ions solution. The percentage of the copper removal was measured by using atomic absorption spectroscopy (AAS). It was found that, the efficiency of the alumina nanoparticles as an adsorbent was not depending on their phases, but might due to the increased of the particle size at higher sintering temperature. The highest percentage of removal 82.1% was obtained when using the alumina sintered at 1200°C.

Carbon fibre-reinforced polymer (CFRP) composite materials play an increasingly important role in modern manufacturing, and they are among the more prominent materials used in aircraft manufacturing today. However, CFRP is highly prone to delamination and other damage when drilled due to it being extremely strong with a good strength-to-weight ratio and high thermal conductivity. Because of this problem and CFRP’s growing importance in aircraft manufacture, research has focused on the entry and exit holes as indicators of damage occurrence during drilling of screws, rivets, and other types of holes. The inside of the hole was neglected in past research and a proper way to quantify the internal side of a hole by combining the entry and exit hole should be included. To fill this gap and improve the use of CFRP, this paper reports a novel technique to measure the holes by using the extension of the adjusted delamination factor (S_FDSR) for drilling thick CFRP composites in order to establish the influence of machining input variables on key output measures, i.e., delamination and other damages. The experimental results showed a significant difference in interpretation of the damage during the analysis. Improvement was made by providing better perspectives of identifying hole defects.

A silver sulfide (Ag₂S) semiconductor photocatalyst film has been successfully synthesized using a solution casting method. To produce the photocatalyst films, two types of Ag₂S powder were used: a commercialized and synthesized powder. For the commercialized powder (CF/comAg₂S), the Ag₂S underwent a rarefaction process to reduce its crystallite size from 52 nm to 10 nm, followed by incorporation into microcrystalline cellulose using a solution casting method under the presence of an alkaline/urea solution. A similar process was applied to the synthesized Ag₂S powder (CF/syntAg₂S), resulting from the co-precipitation process of silver nitrate (AgNO₃) and thiourea. The prepared photocatalyst films and their photocatalytic efficiency were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and UV-visible spectroscopy (UV-Vis). The results showed that the incorporation of the Ag₂S powder into the cellulose films could reduce the peak intensity of the oxygen-containing functional group, which indicated the formation of a composite film. The study of the crystal structure confirmed that all of the as-prepared samples featured a monoclinic acanthite Ag₂S structure with space group P₂₁/C. It was found that the degradation rate of the methylene blue dye reached 100% within 2 h under sunlight exposure when using CF/comAg₂S and 98.6% for the CF/syntAg₂S photocatalyst film, and only 48.1% for the bare Ag₂S powder. For the non-exposure sunlight samples, the degradation rate of only 33–35% indicated the importance of the semiconductor near-infrared (NIR) Ag₂S photocatalyst used.

Dye sensitized solar cell (DSSC) is the third generation solar cell that consists of semiconductor electrode, dye, electrolyte and counter electrode. Among all of the components, dyes perform a primary role in absorbing solar energy and converting it to electrical energy. Therefore, the DSSC performance is absolutely depends on the type of dye sensitizer used. The traditional DSSC used Ruthenium (Ru) complexes as the sensitizer. However, Ru has several limitations due to high cost, rarity and complexity to be synthesized. Thus, in exchange to metal complex Ru dyes, current researches are focusing on natural dyes that are extracted from plants. This paper emphasizes on various researches which involved natural dye pigments; anthocyanin, chlorophyll and betalain. Based on the data comparisons, betalain pigments extracted from purple wild sicilian prickly pear dye has recorded the highest energy conversion efficiency of 2.06%. This has made the betalain pigments as a promising candidate for the best natural dye sensitizer, followed by anthocyanin and chlorophyll.