Polylactic acid (PLA) is a widely used bioresorbable polymer in medical devices owing to its biocompatibility, bioresorbability, and biodegradability. It is also considered a sustainable solution for a wide variety of other applications, including packaging. Because of its widespread use, there have been many studies evaluating this polymer. However, gaps still exist in our understanding of the hydrolytic degradation in extreme pH environments and its impact on physical and mechanical properties, especially in fibrous materials. The goal of this work is to explore the hydrolytic degradation of PLA fibers as a function of a wide range of pH values and exposure times. To complement the experimental measurements, molecular-level details were obtained using both molecular dynamics (MD) simulations with ReaxFF and density functional theory (DFT) calculations. The hydrolytic degradation of PLA fibers from both experiments and simulations was observed to have a faster rate of degradation in alkaline conditions, with 40% of strength loss of the fibers in just 25 days together with an increase in the percent crystallinity of the degraded samples. Additionally, surface erosion was observed in these PLA fibers, especially in extreme alkaline environments, in contrast to bulk erosion observed in molded PLA grafts and other materials, which is attributed to the increased crystallinity induced during the fiber spinning process. These results indicate that spun PLA fibers function in a predictable manner as a bioresorbable medical device when totally degraded at end-of-life in more alkaline conditions.

Sulfur (S) has been considered as a promising cathode candidate for lithium batteries due to its high theoretical specific capacity and energy density. However, the low active material utilization, severe capacity fading, and short lifespan of the resultant lithium–sulfur (Li–S) batteries have greatly hindered their practicality. In this work, a multi-functional polyacrylonitrile/silica nanofiber membrane with an integral ultralight and thin multi-walled carbon nanotube sheet is presented and it provides a new approach to significantly improve the overall electrochemical performance of Li–S batteries. The experimental results are in agreement with molecular modeling studies based on density functional theory and Monte Carlo simulations. Remarkably, this design is favorable for the fast diffusion of both lithium ions and electrons and the mitigation of the diffusion of polysulfides. As a consequence, a high reversible capacity of 741 mA h g⁻¹ at 0.2C after 100 cycles with excellent cyclability and high-rate performance (627 mA h g⁻¹ at 1C) are achieved even with a high sulfur loading of 70 wt% in the cathode, revealing its great potential for energy storage applications. Moreover, a capacity of 426 mA h g⁻¹ is retained after 300 cycles at a high current density of 2C. These results represent a major step forward in the progress of Li–S battery technologies.