A review on lithium niobate single crystals and polycrystals has been prepared. Both the classical and recent literature on this topic is revisited. It is composed of two parts with several sections. The current part discusses the available defect models (intrinsic), the trends found in ion-doped crystals and polycrystals (extrinsic defects), the fundamentals on dilute magnetic oxides, and their connection to ferromagnetic behavior in lithium niobate.

A review of lithium niobate single crystals and polycrystals in the form of powders has been prepared. Both the classical and recent literature on this topic are revisited. It is composed of two parts with sections. The current part discusses the earliest developments in this field. It treats in detail the basic concepts, the crystal structure, some of the established indirect methods to determine the chemical composition, and the main mechanisms that lead to the manifestation of ferroelectricity. Emphasis has been put on the powdered version of this material: methods of synthesis, the accurate determination of its chemical composition, and its role in new and potential applications are discussed. Historical remarks can be found scattered throughout this contribution. Particularly, an old conception of the crystal structure thought as a derivative structure from one of higher symmetry by generalized distortion is here revived.

Nonlinear optical response of Au metallic nanoparticles, synthesized and embedded in sapphire by using ion implantation, as a function of their size and shape is studied. The size of the Au NPs was varied by controlling the annealing time of the gold-irradiated sapphire in a reducing atmosphere. Their shape was changed from approximately spherical to prolate by swift heavy-ion irradiation using Si³⁺, obtaining an anisotropic composite consisting in deformed NPs, all oriented in the direction of the Si beam irradiation. At 532 nm and 26 ps pulses, the isotropic system shows negative nonlinear absorption increasing with size, and positive nonlinear refraction. On the other hand, prolate nanoparticles show negative (null) absorption and null (positive) refraction for the minor (major) axis. This kind of system also shows figures of merit and relaxing times in the order of the picoseconds, appropriate for all-optical switching applications.

In this work, we present a study of the nonlinear absorption properties from different gold nanorod (NR) systems in aqueous suspension. The NRs were obtained with the bottom-up protocol by the seed-mediated growth method (SMG), using Ag⁺ ions at different concentrations, and CTAB as surfactant. By using this method, aspect ratios between 2 and 5 were obtained. The transverse surface plasmons (TSP) are located between 514 – 535 nm, while the longitudinal surface plasmons (LSP) are between 639 – 921 nm, for the different samples studied. The Z-scan technique was implemented for open (OA) and closed (CA) aperture at 532 and 1064 nm, with laser pulses of 26 ps, for vertical and horizontal polarizations, with respect to the incidence plane (horizontal). At 532 nm all samples showed saturable absorption (SA), while for samples with LSP near 1064 nm, such effect was observed only at low-energy pulse experimental conditions. In the high-energy pulse regime, an apparent reverse-saturable absorption (RSA) was observed for both wavelengths. However for 532 nm, it was possible to determine that this effect results from structural changes in the samples, which are manifested through the behavior of nonlinear absorption and refraction curves. These results were used to determine the irradiances to which NRs can be modified by photodegradation.