Coatings, with a thickness of up to 75 µm, were formed by plasma electrolytic oxidation (PEO) under the alternating current electrical mode in a silicate-alkaline electrolyte on aluminum composites without additives and alloyed with copper (1–4.5%). The coatings’ structure was analyzed by scanning electron microscopy, X-ray microanalysis, X-ray photoelectron spectroscopy, nuclear backscattering spectrometry, and XRD analysis. The coatings formed for 60 min were characterized by excessive aluminum content and the presence of low-temperature modifications of alumina γ-Al₂O₃ and η-Al₂O₃. The coatings formed for 180 min additionally contained high-temperature corundum α-Al₂O₃, and aluminum inclusions were absent. The electrochemical behavior of coated composites and uncoated ones in 3% NaCl was studied. Alloyage of aluminum composites with copper increased the corrosion current density. Plasma electrolytic oxidation reduced it several times.

Ceramic-like oxide coatings on zirconium with a thickness of up to 300 μm produced by plasma treatment in an electrolyte demonstrate high thermal resistivity and low thermal conductivity during...