The influence of technological parameters of plasma electrolytic nitriding and polishing on the wear resistance and corrosion resistance of medium-carbon steel is considered. The morphology and roughness of the surface, phase composition and microhardness of the modified layer have been investigated. Wear resistance was studied under dry friction conditions with bearing steel as counter-body. It was found that plasma electrolytic polishing removes the loose part of the oxide layer and provides a two-fold decrease in surface roughness compared with untreated steel, and 2.8 times compared with the nitrided one. Combined processing at optimal technological parameters leads to an increase in microhardness up to 1130 HV, an increase in wear resistance by 70 times, and a decrease in the corrosion current density by almost 3 times in comparison with untreated steel.

The possibility of using an aqueous non-toxic electrolyte of ammonium nitrate and glycerin for the cathodic plasma electrolytic nitrocarburizing of low-carbon steel is considered in this paper. Surface morphology and roughness, element and phase compositions, and microhardness of the modified layer were investigated. Kinetic calculations of the processes of nitrogen and carbon diffusion into the steel surface are proposed, taking into account their mutual influence. Wear resistance was studied under dry friction conditions with tool alloy steel as a counter-body. Corrosion studies are performed using potentiodynamic polarization curves in 3.5% sodium chloride solution. The plasma electrolytic nitrocarburizing in an aqueous electrolyte with ammonium nitrate and glycerin is established to increase surface hardness up to 980 HV due to the formation of a nitrocarburized layer with 1.35 ± 0.12% carbon and 0.32 ± 0.08% nitrogen concentration. The influence of erosion in electrolyte plasma and high-temperature oxidation on the morphology and surface roughness is shown. The presence of a dense oxide layer, low surface roughness, and high hardness of the diffusion layer favor a decrease in the friction coefficient by 1.3 times, weight wear by 1.8 times and corrosion current density by 1.4 times.

The results of modifying the surface of austenitic stainless steel by anodic plasma electrolytic treatment are presented. Surface treatment was carried out in aqueous electrolytes based on ammonium chloride (10%) with the addition of ammonia (5%) as a source of nitrogen (for nitriding), boric acid (3%) as a source of boron (for boriding) or glycerin (10%) as a carbon source (for carburizing). Morphology, surface roughness, phase composition and microhardness of the diffusion layers in addition to the tribological properties were studied. The influence of physicochemical processes during the anodic treatment of the features of the formation of the modified surface and its operational properties are shown. The study revealed the smoothing of irregularities and the reduction in surface roughness during anodic plasma electrolytic treatment due to electrochemical dissolution. An increase in the hardness of the nitrided layers to 1450 HV with a thickness of up to 20–25 μm was found due to the formation of iron nitrides and iron-chromium carbides with a 3.7-fold decrease in roughness accompanied by an increase in wear resistance by 2 orders. The carburizing of the steel surface leads to a smaller increase in hardness (up to 700 HV) but a greater thickness of the hardened layer (up to 80 μm) due to the formation of chromium carbides and a solid solution of carbon. The roughness and wear resistance of the carburized surface change are approximately the same values as after nitriding. As a result of the boriding of the austenitic stainless steel, there is no hardening of the surface, but, at the same time, there is a decrease in roughness and an increase in wear resistance on the surface. It has been established that frictional bonds in the friction process are destroyed after all types of processing as a result of the plastic displacement of the counter body material. The type of wear can be characterized as fatigue wear with boundary friction and plastic contact. The correlation of the friction coefficient with the Kragelsky–Kombalov criterion, a generalized dimensionless criterion of surface roughness, is shown.